Structural and Magnetic Properties of Inverse-Heusler Mn2FeSi Alloy Powder Prepared by Ball Milling
- 1.
SYSNO ASEP 0554684 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Structural and Magnetic Properties of Inverse-Heusler Mn2FeSi Alloy Powder Prepared by Ball Milling Tvůrce(i) Životský, O. (CZ)
Skotnicová, K. (CZ)
Čegan, T. (CZ)
Juřica, J. (CZ)
Gembalová, L. (CZ)
Zažímal, František (UFM-A)
Szurman, I. (CZ)Celkový počet autorů 7 Číslo článku 697 Zdroj.dok. Materials. - : MDPI
Roč. 15, č. 3 (2022)Poč.str. 11 s. Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova transport ; inverse-Heusler alloys ; ball milling ; powders ; microstructure ; Neel temperature ; magnetic transitions Vědní obor RIV BM - Fyzika pevných látek a magnetismus Obor OECD Condensed matter physics (including formerly solid state physics, supercond.) Způsob publikování Open access Institucionální podpora UFM-A - RVO:68081723 UT WOS 000756109000001 EID SCOPUS 85123163079 DOI 10.3390/ma15030697 Anotace Ternary Mn2FeSi alloy was synthesized from pure elemental powders by mechanical alloying, using a high-energy planetary ball mill. The formation of an inverse-Heusler phase after 168 h of milling and subsequent annealing at 1173 K for 1.5 h was confirmed by X-ray diffraction. The diffractogram analysis yielded XA structure and the lattice parameter 0.5677 nm in a good agreement with the theoretically obtained value of 0.560 nm. The final powder was formed by particles of irregular shape and median diameter D50 of 3.8 mu m and their agglomerates. The chemical analysis resulted in the mean composition of 49.0 at.% Mn, 25.6 at.% Fe and 25.4 at.% Si. At room temperature, the prepared samples featured a heterogeneous magnetic structure consisting of dominant paramagnetic phase confirmed by Mossbauer spectrometry and a weak ferro-/ferrimagnetic contribution detected by magnetization curves. From the field-cooled and zero-field-cooled curves the Neel temperature of 67 K was determined. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2023 Elektronická adresa https://www.mdpi.com/1996-1944/15/3/697
Počet záznamů: 1