Influence of the microstructure of the initial material on the Zn wires prepared by direct extrusion with a huge extrusion ratio
- 1.
SYSNO ASEP 0546341 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Influence of the microstructure of the initial material on the Zn wires prepared by direct extrusion with a huge extrusion ratio Tvůrce(i) Čapek, Jaroslav (FZU-D) ORCID
Kadeřávek, Lukáš (FZU-D) ORCID
Pinc, Jan (FZU-D) ORCID
Kopeček, Jaromír (FZU-D) RID, ORCID
Klimša, Ladislav (FZU-D) ORCIDCelkový počet autorů 5 Číslo článku 787 Zdroj.dok. Metals. - : MDPI
Roč. 11, č. 5 (2021)Poč.str. 14 s. Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova Zn-based absorbable materials ; biodegradable materials ; extrusion ; mechanical properties ; microstructure Vědní obor RIV JG - Hutnictví, kovové materiály Obor OECD Materials engineering CEP GA18-06110S GA ČR - Grantová agentura ČR LM2018110 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy EF16_019/0000760 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Způsob publikování Open access Institucionální podpora FZU-D - RVO:68378271 UT WOS 000662682100001 EID SCOPUS 85105731728 DOI 10.3390/met11050787 Anotace In this study, we prepared zinc wires with a diameter of 250 µm by direct extrusion using an extrusion ratio of 576. The wires extruded at 300 ◦C possessed a coarse-grained microstructure and the shape of their tensile stress–strain curves suggested that twinning played an important role during their deformation. A significant influence of the initial grain size on the final microstructure was observed after the extrusion at 100 ◦C. The wires prepared from the billet with a very coarse-grained microstructure possessed a bimodal grain size. A significant coarsening of their microstructure was observed after the tensile test. The wires prepared from the medium-grained billets at 100 ◦C were relatively coarse-grained, but their grain size was stable during the straining, resulting in the highest ultimate tensile strength. This preliminary study shows that strong attention should be paid to the extrusion parameters and the microstructure of the initial billets. Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2022 Elektronická adresa http://hdl.handle.net/11104/0322899
Počet záznamů: 1