High strain-rate compressive testing of filling materials for inter-penetrating phase composites
- 1.
SYSNO ASEP 0509991 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název High strain-rate compressive testing of filling materials for inter-penetrating phase composites Tvůrce(i) Doktor, T. (CZ)
Fíla, T. (CZ)
Zlámal, Petr (UTAM-F) RID, SAI, ORCID
Kytýř, Daniel (UTAM-F) SAI, RID, ORCID
Jiroušek, O. (CZ)Celkový počet autorů 5 Zdroj.dok. Acta Polytechnica CTU Proceedings, 25. - Praha : Czech Technical University in Prague, 2019 / Kytýř D. ; Zlámal P. ; Doktor T. - ISBN 978-80-01-06670-6 Rozsah stran /2019/, s. 21-24 Poč.str. 4 s. Forma vydání Online - E Akce Youth Symposium on Experimental Solid Mechanics /17./ Datum konání 06.06.2019 - 08.06.2019 Místo konání Telč Země CZ - Česká republika Typ akce EUR Jazyk dok. eng - angličtina Země vyd. CZ - Česká republika Klíč. slova interpenetration phase composite ; SHPB ; impact protection filling materials ; strain-rate sensitivity Vědní obor RIV JI - Kompozitní materiály Obor OECD Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics CEP EF16_019/0000766 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Institucionální podpora UTAM-F - RVO:68378297 EID SCOPUS 85078277617 DOI 10.14311/APP.2019.25.0021 Anotace In this study behavior of the selected types of filling material for the inter-penetrating phase composites was tested in compressive loading mode at low and high strain-rates. Three types of the filling material were tested, (i) ordnance gelatin, (ii) low expansion polyurethane foam, and (iii) polyurethane putty. To evaluate their impact energy absorption bulk samples of the selected materials were tested in compression loading mode at strain-rates 1000 s−1 to 4000 s−1. The high strain-rate compressive loading was provided by Split Hopkinson Pressure Bar (SHPB) which was equipped with PMMA bars to enable testing of cellular materials with low mechanical impedance. Based on the comparative measurement response to compression at both low and high strain-rates was analysed. The results show a significant strain-rate sensitivity of the ordnance gelatin and of the polyurethane putty, while strain-rate effect in the polyurethane foam was not observed. Pracoviště Ústav teoretické a aplikované mechaniky Kontakt Kulawiecová Kateřina, kulawiecova@itam.cas.cz, Tel.: 225 443 285 Rok sběru 2020 Elektronická adresa https://ojs.cvut.cz/ojs/index.php/APP/article/view/6015
Počet záznamů: 1