Linear potentiodynamic characterization of ECAPed biocompatible AZ91 magnesium alloy
- 1.
SYSNO ASEP 0479876 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Linear potentiodynamic characterization of ECAPed biocompatible AZ91 magnesium alloy Tvůrce(i) Borko, K. (SK)
Fintová, Stanislava (UFM-A) ORCID
Hadzima, B. (SK)Celkový počet autorů 3 Zdroj.dok. Metallography XVI. - Zürich : Trans tech publications, 2017 / Longauerová M. ; Horňák P. ; Zubko P. - ISSN 0255-5476 - ISBN 978-3-0357-1018-2 Rozsah stran s. 404-408 Poč.str. 5 s. Forma vydání Tištěná - P Akce International Symposium on Metallography and Materials Science /16./ Datum konání 20.04.2016 - 22.04.2016 Místo konání Stará Lesná Země SK - Slovensko Typ akce EUR Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova AZ91 magnesium alloy ; ECAP ; potentiodynamic test Vědní obor RIV JK - Koroze a povrchové úpravy materiálů Obor OECD Coating and films Institucionální podpora UFM-A - RVO:68081723 EID SCOPUS 85016988020 DOI 10.4028/www.scientific.net/MSF.891.404 Anotace Mechanical properties and corrosion resistance of Mg alloys basically depend on their chemical composition. Both the mentioned can be influenced by mechanical or heat treatment. In this work was studied the effect of production technology and resulting microstructure on the corrosion resistance of AZ91 alloy. Corrosion resistance of the alloy (AZ91) was analyzed for material after casting and after treatment by ECAP. Result of ECAP treatment is fine grained microstructure of AZ91 alloy and uniform distributed of present intermetallic phases. Corrosion resistance of the experimental material was analyzed in 0.1 molar solution of NaCl through potentiodynamic tests. The ultra-fine grained microstructure after ECAP results in movement of thermodynamic curves to more positive values of corrosion potential (Ecorr). From thermodynamic point of view, this means, that AZ91 alloy after ECAP has slightly higher corrosion resistance, as AZ91 alloy after casting, however the improvement of corrosion resistance is only minor due to the high reactivity of the magnesium in the corrosion environment. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2018
Počet záznamů: 1