EFFECT OF HIP ON LOW CYCLE FATIGUE OF MAR-M247 AT 900°C
- 1.
SYSNO ASEP 0435004 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název EFFECT OF HIP ON LOW CYCLE FATIGUE OF MAR-M247 AT 900°C Tvůrce(i) Šulák, Ivo (UFM-A) ORCID
Obrtlík, Karel (UFM-A) RID, ORCID
Škorík, Viktor (UFM-A) RID
Hrbáček, K. (CZ)Celkový počet autorů 4 Zdroj.dok. METAL 2014: 23rd International Conference on Metallurgy and Materials. - Ostrava : Tanger Ltd, 2014 - ISBN 978-80-87294-52-9 Poč.str. 6 s. Forma vydání Nosič - C Akce METAL 2014. International Conference on Metallurgy and Materials /22./ Datum konání 21.05.2014-23.05.2014 Místo konání Brno Země CZ - Česká republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. CZ - Česká republika Klíč. slova MAR-M-247 ; High temperature ; Low cycle fatigue Vědní obor RIV JL - Únava materiálu a lomová mechanika CEP EE2.3.30.0063 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Institucionální podpora UFM-A - RVO:68081723 UT WOS 000350641700229 Anotace Polycrystalline nickel-base superalloy MAR-M247 is used for high temperature applications requiring excellent combination of fatigue properties, creep resistance and surface stability. These superior high temperature characteristics derive from the microstructure which habitually consists of face centred cubic matrix γ and precipitate γ´ (L12 type ordered structure). In the present work, the high temperature low cycle fatigue behaviour of cast nickel-base superalloy MAR-M247 in as received condition and in hot isostatically pressed (HIP) condition was studied. The microstructure of the materials is characterized by dendritic grains, carbides and casting defects. Distribution and size of defects in both materials were studied. Isothermal low cycle fatigue (LCF) tests were performed on cylindrical specimens under total strain control at 900°C in air. Cyclic stress–strain response and fatigue life of both materials were assessed. Beneficial effects of HIP process on cyclic stress-strain and fatigue life curves are discussed. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2015
Počet záznamů: 1