Fatigue crack initiation in Inconel 713LC at high temperature

0047327 - ÚFM 2007 RIV SK eng C - Konferenční příspěvek (zahraniční konf.)
Mintách, Rastislav - Kunz, Ludvík - Svoboda, Milan
Fatigue crack initiation in Inconel 713LC at high temperature.
[Iniciace únavové trhliny v Inconelu 713LC za vysoké teploty.]
Fractography 2006. Košice: Institute of Mater. Res., Slovak Academy of Sci, 2006 - (Parilák, L.), s. 140-147. ISBN 80-968543-5-6.
[Fractography 2006. Stará Lesná (SK), 15.10.2006-18.10.2006]
Grant CEP: GA ČR GA106/05/2112
Výzkumný záměr: CEZ:AV0Z20410507
Klíčová slova: IN713LC * Fatigue * Crack initiation
Kód oboru RIV: JG - Hutnictví, kovové materiály

Cast Ni base superalloys are known by long Stage I fatigue crack initiation, long early crystallographic fatigue crack propagation and inherent casting defects. These phenomena are closely related to the scatter of experimental fatigue life data. Fatigue crack initiation in high-cycle region and its relation to casting defects was studied in cast IN 713 LC superalloy at tensile mean stress at 800°C in air. Three types of crack initiation were observed. The mechanism of crystallographic initiation is discussed in terms of cyclic strain localization in persistent slip bands.

Lité niklové slitiny jsou známé dlouhým stádiem I iniciace únavových trhlin, dlouhým počátečním krystalografickým šířením trhlin a přítomností licích defektů. Tyto skutečnosti jsou úzce spojeny s velkým rozptylem experimentálních dat při stanovování únavové životnosti. Příspěvek uvádí výsledky studia iniciace únavových trhlin v lité superslitině IN713LC ve vysokocyklové oblasti při 800°C a namáhání na vzduchu. Byly pozorovány tři odlišné typy iniciace. V práci je diskutován mechanizmus krystalografické iniciace ve smyslu lokalizace cyklické plastické deformace v persistentních skluzových pásech.