Epitaxial growth of thin films of X-type Sr2Co2Fe28O46 hexaferrite by chemical solution deposition
- 1.
SYSNO ASEP 0574981 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Epitaxial growth of thin films of X-type Sr2Co2Fe28O46 hexaferrite by chemical solution deposition Tvůrce(i) Soroka, Miroslav (UACH-T) SAI, ORCID, RID
Buršík, Josef (UACH-T) RID, ORCID, SAI
Kužel, R. (CZ)
Horák, L. (CZ)
Prokleška, J. (CZ)
Vronka, M. (CZ)
Laguta, V. (CZ)Celkový počet autorů 7 Zdroj.dok. Journal of the European Ceramic Society. - : Elsevier - ISSN 0955-2219
Roč. 43, č. 15 (2023), s. 6916-6924Poč.str. 9 s. Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova Chemical solution deposition ; Spin reorientation transition ; Thin films ; X-type hexaferrites ; Sr2Co2Fe28O46 Obor OECD Inorganic and nuclear chemistry CEP GA19-06433S GA ČR - Grantová agentura ČR LM2018124 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Výzkumná infrastruktura CzechNanoLab II - 90251 - Vysoké učení technické v Brně / Středoevropský technologický institut Způsob publikování Omezený přístup Institucionální podpora UACH-T - RVO:61388980 UT WOS 001062632400001 EID SCOPUS 85165422168 DOI 10.1016/j.jeurceramsoc.2023.07.027 Anotace Although single crystals of hexaferrites have received considerable attention, the same does not apply for thin films. Here, the growth of epitaxial thin films of Sr2Co2Fe28O46 on a SrTiO3(111) by a chemical solution deposition method is reported. Using X-ray diffraction analysis, the orientation relationship between film and substrate was established as (000l)X || (111)STO and 112̅0X || 101̅STO. The magnetization and magnetic domain structure were investigated using magnetic measurements and Lorentz transmission electron microscopy, respectively. With changing temperature, the magnitude of magnetization in the (0001) plane changed at ∼355 K, while that along the [0001] direction remained almost unchanged, suggesting a spin reorientation transition. Using the ferromagnetic resonance method, it was shown that the compound exhibits a change in the orientation of the magnetic anisotropy in the (0001) plane at ∼ 150 K that supports the occurrence of the multiaxial anisotropy state in film similar to that in single crystals. Pracoviště Ústav anorganické chemie Kontakt Jana Kroneislová, krone@iic.cas.cz, Tel.: 311 236 931 Rok sběru 2024 Elektronická adresa https://doi.org/10.1016/j.jeurceramsoc.2023.07.027
Počet záznamů: 1