Exceptionally small Young modulus in 10M martensite of Ni-Mn-Ga exhibiting magnetic shape memory effect
- 1.0574614 - FZÚ 2024 RIV GB eng J - Článek v odborném periodiku
Cejpek, P. - Drozdenko, D. - Máthis, K. - Colman, R.H. - Dopita, M. - Straka, Ladislav - Heczko, Oleg
Exceptionally small Young modulus in 10M martensite of Ni-Mn-Ga exhibiting magnetic shape memory effect.
Acta Materialia. Roč. 257, Sept. (2023), č. článku 119133. ISSN 1359-6454. E-ISSN 1873-2453
Grant CEP: GA ČR(CZ) GA21-06613S
Institucionální podpora: RVO:68378271
Klíčová slova: magnetic shape memory * martensitic transformation * elastic properties * young modulus * mechanical testing * Ni-Mn-Ga
Obor OECD: Condensed matter physics (including formerly solid state physics, supercond.)
Impakt faktor: 8.3, rok: 2023
Způsob publikování: Omezený přístup
https://doi.org/10.1016/j.actamat.2023.119133
A Ni50Mn28Ga22 single crystal exhibiting 10M martensitic structure at room temperature was studied by X-ray diffraction measured in situ under uniaxial tensile stress up to 20 MPa and in different initial orientations of the sample. When the c axis lies along the direction of the applied stress, the sample is elongated primarily by the stress-induced reorientation. In comparison, with a or b axis lying along the stress direction, the overall elongation happens primarily due to the change of the lattice parameters and also the modulation amplitude of 10M martensite rapidly decreases with the applied tension. The initial tensile Young modulus calculated from the refined lattice parameters is very low and exhibits gradual stiffening with the increasing tensile stress. Close to zero stress the modulus has an extremely low value of about 0.3 GPa.