Microstructure and failure processes of reactor pressure vessel austenitic cladding
- 1.
SYSNO ASEP 0547942 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Microstructure and failure processes of reactor pressure vessel austenitic cladding Tvůrce(i) Štefan, Jan (UT-L) ORCID, RID
Siegl, J. (CZ)
Adámek, J. (CZ)
Kopřiva, R. (CZ)
Falcník, M. (CZ)Celkový počet autorů 5 Číslo článku 1676 Zdroj.dok. Metals. - : MDPI - ISSN 2075-4701
Roč. 11, č. 11 (2021)Poč.str. 10 s. Forma vydání Online - E Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova nuclear reactor pressure vessel ; austenitic cladding ; weld overlay ; fracture toughness test ; fractography ; metallography Vědní obor RIV JL - Únava materiálu a lomová mechanika Obor OECD Materials engineering CEP EF15_003/0000493 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Způsob publikování Open access Institucionální podpora UT-L - RVO:61388998 UT WOS 000727079500001 EID SCOPUS 85117359122 DOI https://doi.org/10.3390/met11111676 Anotace This paper is dedicated to an experimental program focused on the evaluation of microstructure and failure mechanisms of WWER 440 type nuclear reactor pressure vessel cladding made from Sv 08Kh19N10G2B stainless steel. Static fracture toughness tests performed on standard precracked single edge bend specimens revealed extreme variations in fracture toughness values, J0.2.
Fractured halves of test specimens were subject to detailed fractographic and metallographic analyses in order to identify the causes of this behavior and to determine the relationship between local
microstructure, failure mode and fracture toughness. Results indicated that fracture toughness of the cladding was adversely affected by the brittle cracking of sigma particles which caused a considerable decrease in local ductile tearing resistance. Extreme variations in relative amounts of sigma phase, as well as the extreme overall structural heterogeneity of the cladding determined in individual specimens, provided a reasonable explanation for variations in fracture toughness values.Pracoviště Ústav termomechaniky Kontakt Marie Kajprová, kajprova@it.cas.cz, Tel.: 266 053 154 ; Jana Lahovská, jaja@it.cas.cz, Tel.: 266 053 823 Rok sběru 2022 Elektronická adresa https://www.mdpi.com/journal/metals