Application of SPS consolidation and its influence on the properties of the FeAl.sub.20./sub.Si.sub.20./sub. alloys prepared by mechanical alloying

Průša, F.; Šesták, J.; Školáková, A.; Novák, P.; Haušild, P.; Karlík, M.; Minařík, P.; Kopeček, Jaromír; Laufek, F.

doi:https://dx.doi.org/10.1016/j.msea.2019.06.030

Počet záznamů: 1

Application of SPS consolidation and its influence on the properties of the FeAl.sub.20./sub.Si.sub.20./sub. alloys prepared by mechanical alloying

1.

SYSNO ASEP	0521280
Druh ASEP	J - Článek v odborném periodiku
Zařazení RIV	J - Článek v odborném periodiku
Poddruh J	Článek ve WOS
Název	Application of SPS consolidation and its influence on the properties of the FeAl₂₀Si₂₀ alloys prepared by mechanical alloying
Tvůrce(i)	Průša, F. (CZ) Šesták, J. (CZ) Školáková, A. (CZ) Novák, P. (CZ) Haušild, P. (CZ) Karlík, M. (CZ) Minařík, P. (CZ) Kopeček, Jaromír (FZU-D)_{RID, ORCID} Laufek, F. (CZ)
Celkový počet autorů	9
Číslo článku	138020
Zdroj.dok.	Materials Science and Engineering A Structural Materials Properties Microstructure and Processing. - : Elsevier - ISSN 0921-5093 Roč. 761, Jul (2019), s. 1-12
Poč.str.	12 s.
Jazyk dok.	eng - angličtina
Země vyd.	CH - Švýcarsko
Klíč. slova	electron microscopy ; stress/strain measurements ; X-ray analysis ; intermetallics ; nanocrystalline materials ; powder methods
Vědní obor RIV	JG - Hutnictví, kovové materiály
Obor OECD	Materials engineering
CEP	GA17-07559S GA ČR - Grantová agentura ČR
Způsob publikování	Omezený přístup
Institucionální podpora	FZU-D - RVO:68378271
UT WOS	000477784900021
EID SCOPUS	85067832586
DOI	10.1016/j.msea.2019.06.030
Anotace	The FeAl20Si20 alloy was prepared by a combination of short-term mechanical alloying and spark plasma sintering. The processing parameters either of the mechanical alloying or spark plasma sintering were optimized to yield the maximal mechanical properties of the alloy. For the mechanical alloying, two amounts of powders batch (5 g or 20 g) were compared. The spark plasma sintering regimes combined pre-pressing prior heating and vice versa, direct and pulse current flow. The MA + SPS alloys exhibited ultrafine-grained microstructure composed of FeSi, Fe3Si and Fe3Al2Si3 phases (with an average crystallite size of approximately 30 nm) with a presence of randomly distributed Al2O3 particles (with diameters ranging from 5 to 100 nm).
Pracoviště	Fyzikální ústav