HYDROGEN SORPTION IN ORDERED Mg-In ALLOYS
- 1.
SYSNO ASEP 0511641 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název HYDROGEN SORPTION IN ORDERED Mg-In ALLOYS Tvůrce(i) Čermák, Jiří (UFM-A) RID, ORCID
Král, Lubomír (UFM-A) RID, ORCID
Roupcová, Pavla (UFM-A) RID, ORCIDCelkový počet autorů 3 Zdroj.dok. Metal 2019 - 28th International Conference on Metallurgy and Materials. - Ostrava : TANGER Ltd., Ostrava, 2019 - ISBN 978-80-87294-92-5 Rozsah stran s. 1422-1427 Poč.str. 6 s. Forma vydání Nosič - C Akce METAL 2019. International conference on metallurgy and materials /28./ Datum konání 22.05.2019 - 24.05.2019 Místo konání Brno Země CZ - Česká republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. CZ - Česká republika Klíč. slova Hydrogen storage ; Mg alloys ; hydride stability ; ordering Vědní obor RIV JJ - Ostatní materiály Obor OECD Materials engineering CEP LQ1601 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy GA17-21683S GA ČR - Grantová agentura ČR Institucionální podpora UFM-A - RVO:68081723 UT WOS 000539487400233 EID SCOPUS 85079428052 Anotace Hydrogen storage (HS) performance of three Mg- x In- y CB alloys (CB - amorphous carbon, x = 55, 64, 73 y =
10 wt%) was studied. Indium concentration covered an area of ordered β structures. Alloys were prepared by
ball-milling in hydrogen atmosphere. Kinetic curves and PCT isotherms were measured in the temperature
interval from 200 °C to 325 °C. X-ray diffraction spectroscopy (XRD) was used for structure investigation. Alloy
with x = 73 wt% In ( β ’’ structure) showed reversible amorphization during temperature cycling between about
100 °C and 350 °C. Hydrogen sorption experiments were done by the Sieverts method under the hydrogen
gas pressure ranging from 0.1 MPa to 2.5 MPa. It was found that hydrogen sorption capacity varied between
0.47 and 1.1 wt% H 2 . Hydride formation enthalpy ∆H calculated from desorption PCT experiments was
significantly lower than ∆H , known for pure Mg. This invoked an idea that atomic order of Mg-based HS
materials might decrease the high thermodynamic stability of hydride phase.Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2021