Počet záznamů: 1
Dielectric analysis of halloysite nanotubes LLDPE nanocomposite compounds
- 1.
SYSNO ASEP 0461495 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Dielectric analysis of halloysite nanotubes LLDPE nanocomposite compounds Tvůrce(i) Čermák, M. (CZ)
Kadlec, P. (CZ)
Kruliš, Zdeněk (UMCH-V) RID, ORCID
Polanský, R. (CZ)Zdroj.dok. AIP Conference Proceedings 1713. - Melville : American Institute of Physics, 2016 / Rhee B. - ISSN 0094-243X - ISBN 978-0-7354-1360-3 Rozsah stran 090007_1-090007_5 Poč.str. 5 s. Forma vydání Tištěná - P Akce International Conference of the Polymer-Processing-Society /31./ - PPS-31 Datum konání 07.06.2015 - 11.06.2015 Místo konání Jeju Island Země KR - Korejská republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova halloysite nanotube ; polymer nanocomposite ; polarization Vědní obor RIV CD - Makromolekulární chemie Institucionální podpora UMCH-V - RVO:61389013 UT WOS 000375945000047 EID SCOPUS 84984586750 DOI 10.1063/1.4942303 Anotace The aim of this paper is to investigate the influence of HNT on the dielectric properties of LLDPE (linear low density polyethylene) nanocomposite compounds in the different level of fulfillment (0, 1, 3. 7 wt%). The utilization of these HNT/LLDPE nanocomposite compounds can be seen in the cable industry. where the dielectric properties are essential. Used experimental compounds have been prepared in the laboratory blades mixer Brabender W50 EHT and the plasticorder Brabender PLE 651. immediately after mixing, the molten compounds were removed front the mixer, inserted into the spacer, and pressed into films of 0.25 mm thickness. Dielectric properties in the DC field (polarization current, reading of polarization index, volume resistivity) of the individual samples were measured and the temperature and frequency range by Broadband dielectric spectroscopy Alpha-A (Novocontrol) were investigated. Samples have been subjected to the dielectric strength test according to standards. As results showed, experimental samples were affected by HNT, especially in the dielectric relaxation phenomena, when during the increment of the level of fulfilment occurred the increasing of the nearly lossless dielectric relaxations. The volume resistivity of the samples was affected in the range of one magnitude. Pracoviště Ústav makromolekulární chemie Kontakt Eva Čechová, cechova@imc.cas.cz ; Tel.: 296 809 358 Rok sběru 2017
Počet záznamů: 1