Estimation of the Plastic Zone in Fatigue via Micro-Indentation

  1. 1.
    SYSNO ASEP0546422
    Druh ASEPJ - Článek v odborném periodiku
    Zařazení RIVJ - Článek v odborném periodiku
    Poddruh JČlánek ve WOS
    NázevEstimation of the Plastic Zone in Fatigue via Micro-Indentation
    Tvůrce(i) Lopez-Crespo, C. (ES)
    Crupes, A.S. (ES)
    Seitl, Stanislav (UFM-A) RID, ORCID
    Moreno, B. (ES)
    Lopez-Crespo, P. (ES)
    Celkový počet autorů5
    Číslo článku5885
    Zdroj.dok.Materials. - : MDPI
    Roč. 14, č. 19 (2021)
    Poč.str.14 s.
    Jazyk dok.eng - angličtina
    Země vyd.CH - Švýcarsko
    Klíč. slovaplastic zone in fatigue cracks ; fatigue of materials ; micro-indentation
    Vědní obor RIVJN - Stavebnictví
    Obor OECDCivil engineering
    CEPGA20-00761S GA ČR - Grantová agentura ČR
    Způsob publikováníOpen access
    Institucionální podporaUFM-A - RVO:68081723
    UT WOS000707739400001
    EID SCOPUS85117027984
    DOI10.3390/ma14195885
    AnotaceAccurate knowledge of the plastic zone of fatigue cracks is a very direct and effective way to quantify the damage of components subjected to cyclic loads. In this work, we propose an ultra-fine experimental characterisation of the plastic zone based on Vickers micro-indentations. The methodology is applied to different compact tension (CT) specimens made of aluminium alloy 2024-T351 subjected to increasing stress intensity factors. The experimental work and sensitivity analysis showed that polishing the surface to #3 μm surface finish and applying a 25 g-force load for 15 s produced the best results in terms of resolution and quality of the data. The methodology allowed the size and shape of both the cyclic and the monotonic plastic zones to be visualised through 2D contour maps. Comparison with Westergaard’s analytical model indicates that the methodology, in general, overestimates the plastic zone. Comparison with S355 low carbon steel suggests that the methodology works best for alloys exhibiting a high strain hardening ratio.
    PracovištěÚstav fyziky materiálu
    KontaktYvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485
    Rok sběru2022
    Elektronická adresahttps://www.mdpi.com/1996-1944/14/19/5885
Počet záznamů: 1  

  Tyto stránky využívají soubory cookies, které usnadňují jejich prohlížení. Další informace o tom jak používáme cookies.