Calculations of Avrami exponent and applicability of Johnson-Mehl-Avrami model on crystallization in Er:LiY(PO.sub.3./sub.).sub.4./sub. phosphate glass
- 1.
SYSNO ASEP 0536253 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Calculations of Avrami exponent and applicability of Johnson-Mehl-Avrami model on crystallization in Er:LiY(PO3)4 phosphate glass Tvůrce(i) Zemenová, Petra (FZU-D) RID, ORCID
Král, Robert (FZU-D) RID, ORCID
Rodová, Miroslava (FZU-D)
Nitsch, Karel (FZU-D) RID
Nikl, Martin (FZU-D) RID, ORCID, SAICelkový počet autorů 5 Zdroj.dok. Journal of Thermal Analysis and Calorimetry. - : Akadémiai Kiadó - ISSN 1388-6150
Roč. 141, č. 3 (2020), s. 1091-1099Poč.str. 9 s. Jazyk dok. eng - angličtina Země vyd. HU - Maďarsko Klíč. slova phosphate glass ; nucleation ; crystallization ; DSC ; Avrami exponent ; JMA model Vědní obor RIV BM - Fyzika pevných látek a magnetismus Obor OECD Materials engineering CEP EF16_013/0001406 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy LO1409 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy LM2015088 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Způsob publikování Omezený přístup Institucionální podpora FZU-D - RVO:68378271 UT WOS 000557765400002 EID SCOPUS 85075967915 DOI 10.1007/s10973-019-09068-w Anotace Preparation and thermal properties of Er3+- doped lithium–yttrium meta-phosphate glasses with a nominal composition of Er:LiY(PO3)4 were studied as a new scintillating material for neutron detection. The glassy Er:LiY(PO3)4 ingots 10 × 10 × 25 mm3 in size were prepared by quenching of the molten mixture of the starting lithium carbonate, yttrium phosphate, and phosphorus oxide in stoichiometric relations. Crystallization kinetics was experimentally studied on powder samples with particle sizes ranging from 96 to 106 μm, 200 to 212 μm, and on bulk glassy samples using the non-isothermal differential scanning calorimetry. The evaluation of the measured data was performed using the Johnson–Mehl–Avrami, Matusita and Augis–Bennett models, and the y(α) and z(α) functions. Obtained kinetic parameters were used for reconstruction of the crystallization peaks using various models and compared with actual experimental data. Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2021 Elektronická adresa https://doi.org/10.1007/s10973-019-09068-w
Počet záznamů: 1