Influence of processing on the microstructure and the mechanical properties of Zn/HA8 wt.% biodegradable composite
- 1.
SYSNO ASEP 0519318 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve SCOPUS Název Influence of processing on the microstructure and the mechanical properties of Zn/HA8 wt.% biodegradable composite Tvůrce(i) Pinc, Jan (FZU-D) ORCID
Miklášová, E. (CZ)
Průša, F. (CZ)
Čapek, Jaroslav (FZU-D) ORCID
Drahokoupil, Jan (FZU-D) RID, ORCID
Vojtěch, D. (CZ)Celkový počet autorů 6 Zdroj.dok. Manufacturing Technology, Journal for Science, Research and Production. - : Univerzita J. E. Purkyně - ISSN 1213-2489
Roč. 19, č. 5 (2019), s. 836-841Poč.str. 6 s. Jazyk dok. eng - angličtina Země vyd. CZ - Česká republika Klíč. slova zinc ; hydroxyapatite ; biodegradable composites ; ball milling ; spark plasma sintering Vědní obor RIV JI - Kompozitní materiály Obor OECD Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics CEP GA18-06110S GA ČR - Grantová agentura ČR Způsob publikování Omezený přístup Institucionální podpora FZU-D - RVO:68378271 EID SCOPUS 85077169193 DOI 10.21062/ujep/381.2019/a/1213-2489/MT/19/5/836 Anotace Zinc-based materials show large potential to become biodegradable materials with ideal corrosion behavior in the body environment. In this study, a zinc composite containing 8 wt. % of hydroxyapatite (HA) was prepared by spark plasma sintering (SPS) and characterized from a point of view of the microstructural and mechanical prop-erties. The influence of pre-processing (milling) of the powders on the microstructure after the sintering was stud-ied. The materials prepared by the milling and subsequent sintering showed insufficient cohesion due to the wrap-ping of Zn by HA particles and possible oxidation of zinc particles. Compressive and flexural tests of sintered materials prepared without any pre-processing confirmed the role of hydroxyapatite as a defect in the Zn/HA8_SPS structure. The results of the hardness measurement suggest that the HA does not affect the behavior of the zinc matrix. Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2020 Elektronická adresa https://doi.org/10.21062/ujep/381.2019/a/1213-2489/MT/19/5/836
Počet záznamů: 1