Thermo-mechanical and isothermal fatigue behavior of austenitic stainless steel AISI 316L
- 1.
SYSNO ASEP 0449806 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Thermo-mechanical and isothermal fatigue behavior of austenitic stainless steel AISI 316L Tvůrce(i) Škorík, Viktor (UFM-A) RID
Šulák, Ivo (UFM-A) ORCID
Obrtlík, Karel (UFM-A) RID, ORCID
Polák, Jaroslav (UFM-A) RID, ORCIDCelkový počet autorů 4 Zdroj.dok. Metal 2015: 24th International Conference on Metallurgy and Materials. - Ostrava : TANGER Ltd, 2015 - ISBN 978-80-87294-58-1 Poč.str. 6 s. Forma vydání Nosič - C Akce METAL 2015 - International Conference on Metallurgy and Materials /24./ Datum konání 03.06.2015-05.06.2015 Místo konání Brno Země CZ - Česká republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. CZ - Česká republika Klíč. slova Thermo-mechanical fatigue (TMF) ; In-phase cycling (IP) ; Isothermal fatigue (IF) ; AISI 316L ; Fatigue life Vědní obor RIV JL - Únava materiálu a lomová mechanika CEP EE2.3.30.0063 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy GA15-20991S GA ČR - Grantová agentura ČR GA13-23652S GA ČR - Grantová agentura ČR Institucionální podpora UFM-A - RVO:68081723 UT WOS 000374706100136 Anotace Many structural components of nuclear power plant systems are made of austenitic stainless steels. These structures undergo degradation by thermo-mechanical fatigue (TMF) caused by simultaneous cyclic straining and temperature cycling, particularly during start-up, shut-down and transient operations. The present work reports the cyclic deformation behavior and fatigue damage of austenitic stainless steel AISI 316L during TMF and isothermal fatigue (IF) testing in air. Total strain controlled in-phase TMF loading in the temperature range 200 - 600 °C and isothermal fatigue (IF) at 600 °C were performed. Hardening/softening curves, cyclic stress-strain response and fatigue life diagrams were obtained both for TMF and IF tests. Fatigue damage was documented using surface relief and fracture surface observations. Mean stress evolution and fatigue degradation data are employed to discuss the fatigue behavior of 316L steel both in TMF and IF regimes. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2016
Počet záznamů: 1