Root cause of embrittlement of in-service exposed high pressure steam pipeline
- 1.
SYSNO ASEP 0570444 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Root cause of embrittlement of in-service exposed high pressure steam pipeline Tvůrce(i) Ohanková, M. (CZ)
Čmakal, J. (CZ)
Junek, M. (CZ)
Kvapilová, Marie (UFM-A) RID, ORCID
Dvořák, Jiří (UFM-A) RID, ORCID
Sklenička, Václav (UFM-A) RID, ORCIDCelkový počet autorů 6 Zdroj.dok. Procedia Structural Integrity, Materials Structure & Micromechanics of Fracture, 43. - Amsterdam : Elsevier B. V., 2023 / Pokluda J. ; Šandera P. - ISSN 2452-3216 Rozsah stran s. 300-305 Poč.str. 6 s. Forma vydání Online - E Akce MSMF10 - International Conference on Materials Structure and Micromechanics of Fracture /10./ Datum konání 12.09.2022 - 14.09.2022 Místo konání Brno Země CZ - Česká republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova Steam pipeline ; embrittlement ; microstructure ; mechanical properties ; heat treatment ; low-alloyed steel Vědní obor RIV JG - Hutnictví, kovové materiály Obor OECD Materials engineering CEP TK03020089 GA TA ČR - Technologická agentura ČR Institucionální podpora UFM-A - RVO:68081723 UT WOS 001198152000050 EID SCOPUS 85159792856 DOI https://doi.org/10.1016/j.prostr.2022.12.275 Anotace A segment of tube cut off from the high pressure steam pipeline was subjected to routine basic material tests, which resulted in very low impact energy of the pipe material (low-alloyed Cr steel). A part of the segment (and a comparative non-operated sample) was then subjected to detailed mechanical tests (including creep), metallographic investigations and fractographic analyses with an aim to determine a root cause of the embrittlement. The results showed that grain boundaries of exposed steel are covered by particles of primary and secondary cementite. However, a matrix is weakened more, therefore a fracture of creep, tensile and impact specimens is always transgranular and the cleavage facets are limited to grain size, if present. Thus, the cause of embrittlement was determined not by a rapid ageing, but by an unsuitable initial heat treatment of the pipe material. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2024
Počet záznamů: 1