Performance of Sc-Y-ODS variant of Eurofer steel in stagnant PbLi at 600 C
- 1.
SYSNO ASEP 0570262 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Performance of Sc-Y-ODS variant of Eurofer steel in stagnant PbLi at 600 C Tvůrce(i) Hojná, A. (CZ)
Pazderova, M. (CZ)
Rozumová, L. (CZ)
Vít, J. (CZ)
Hadraba, Hynek (UFM-A) RID, ORCID
Stratil, Luděk (UFM-A) ORCID
Čížek, Jan (UFP-V) ORCIDCelkový počet autorů 7 Číslo článku 154227 Zdroj.dok. Journal of Nuclear Materials. - : Elsevier - ISSN 0022-3115
Roč. 575, MAR (2023)Poč.str. 13 s. Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova Fusion ; Liquid leadlithium ; Ferritic-martensitic steel ; Oxide dispersionstrengthened steel ; Corrosion ; Microstructure ; Mechanical behavior Vědní obor RIV JG - Hutnictví, kovové materiály Obor OECD Materials engineering Vědní obor RIV – spolupráce Ústav fyziky plazmatu - Průmyslové procesy a zpracování CEP GA20-20873S GA ČR - Grantová agentura ČR Způsob publikování Omezený přístup Institucionální podpora UFM-A - RVO:68081723 ; UFP-V - RVO:61389021 UT WOS 000923597300001 EID SCOPUS 85145777762 DOI 10.1016/j.jnucmat.2022.154227 Anotace This paper represents a part of the research of structural materials for fusion systems. The performance of a conventionally formed Eurofer-97 steel and its Sc-Y-ODS variant developed by our group was assessed in a stagnant liquid PbLi environment. The experiments were performed at 60 0 degrees C for 50 0 and 10 0 0 hours, and the subsequent microscopical investigation identified a solution-based attack as the dominant corro-sion damage of both materials. The metal loss of the conventional Eurofer-97 steel was 66.2 pm after 10 0 0 h exposure, corresponding to a rate of 580 pm/year. In contrast, the ODS Eurofer variant strength-ened with various fine Sc-Y complex oxides showed a 70% lower corrosion damage, mainly owing to formation of a Sc-Y-rich Pb surface layer. To understand the degradation process in more detail, both materials were characterized before and after the PbLi exposure in terms of their microstructures and mechanical behavior including hardness, tensile, impact and static fracture toughness tests.(c) 2022 Elsevier B.V. All rights reserved. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2024 Elektronická adresa https://www.sciencedirect.com/science/article/pii/S0022311522007061?via%3Dihub
Počet záznamů: 1