Corrosion and Electrochemical Properties of Laser-Shock-Peening-Treated Stainless Steel AISI 304L in VVER Primary Water Environment
- 1.
SYSNO ASEP 0565486 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Corrosion and Electrochemical Properties of Laser-Shock-Peening-Treated Stainless Steel AISI 304L in VVER Primary Water Environment Tvůrce(i) Arnoult, Xavier (UT-L)
Arnoult-Růžičková, M. (CZ)
Maňák, Jan (FZU-D) ORCID
Viani, Alberto (UTAM-F) RID, ORCID, SAI
Brajer, Jan (FZU-D) ORCID
Arrigoni, M. (FR)
Kolman, Radek (UT-L) RID
Macák, J. (CZ)Celkový počet autorů 8 Číslo článku 1702 Zdroj.dok. Metals. - : MDPI
Roč. 12, č. 10 (2022)Poč.str. 16 s. Forma vydání Online - E Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova corrosion ; electrochemical impedance spectroscopy ; high-temperature water ; laser shock processing ; plastic deformation ; shock wave ; surface treatment Vědní obor RIV CG - Elektrochemie Obor OECD Nuclear related engineering Vědní obor RIV – spolupráce Fyzikální ústav - Fyzika pevných látek a magnetismus
Ústav teoretické a aplikované mechaniky - Inženýrské stavitelstvíCEP EF15_003/0000493 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy EF15_006/0000674 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy GF22-00863K GA ČR - Grantová agentura ČR Způsob publikování Open access Institucionální podpora UT-L - RVO:61388998 ; FZU-D - RVO:68378271 ; UTAM-F - RVO:68378297 UT WOS 000874365500001 EID SCOPUS 85140872984 DOI 10.3390/met12101702 Anotace Laser Shock Peening (LSP) is a surface treatment technique for metallic materials. It induces plastic deformation at the surface of up to around 1 mm in depth. This process introduces residual stresses that lead to strain hardening, and potentially improvements in fatigue, stress corrosion cracking (SCC) and general corrosion behaviour in many, but not all, corrosive media. In this paper, two specimens made of AISI 304L stainless steel, one LSP-treated and one un-treated, were tested at 280 °C and 8 MPa in VVER (or PWR) primary circuit water chemistry using in situ Electrochemical Impedance Spectroscopy (EIS). This experiment serves to qualify the influence of LSP on the changes in corrosion behaviour in high-temperature, high-density water. The residual stress (RS) measurement of the surface showed a compression RS. Before LSP treatment, RS at the surface was 52.2 MPa in the rolling direction 0°RD and 10.42 MPa in the transverse rolling direction 90°RD. After the treatment, surface RS was −175.27 MPa and −183.51 MPa for Scan and TScan directions, respectively. The effect of compressive RS at the surface was studied and showed an increase in corrosion rate. The analysis of oxide layer by SEM revealed differences between LSP-treated and untreated AISI 304L specimens and their connection to corrosion rates. Pracoviště Ústav termomechaniky Kontakt Marie Kajprová, kajprova@it.cas.cz, Tel.: 266 053 154 ; Jana Lahovská, jaja@it.cas.cz, Tel.: 266 053 823 Rok sběru 2023 Elektronická adresa https://mdpi-res.com/d_attachment/metals/metals-12-01702/article_deploy/metals-12-01702.pdf?version=1665563594
Počet záznamů: 1