Nanotwinned (inter)martensite transformation interfaces in Ni.sub.50./sub.Mn.sub.25./sub.Ga.sub.20./sub.Fe.sub.5./sub. magnetic shape memory single crystal foil
- 1.
SYSNO ASEP 0561686 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Nanotwinned (inter)martensite transformation interfaces in Ni50Mn25Ga20Fe5 magnetic shape memory single crystal foil Tvůrce(i) Ge, Yanling (FZU-D) ORCID
Straka, Ladislav (FZU-D) ORCID
Vronka, Marek (FZU-D) ORCID, RID
Rameš, Michal (FZU-D) RID, ORCID
Sozinov, A. (FI)
Heczko, Oleg (FZU-D) RID, ORCIDCelkový počet autorů 6 Číslo článku 112007 Zdroj.dok. Materials Characterization. - : Elsevier - ISSN 1044-5803
Roč. 190, Aug (2022)Poč.str. 13 s. Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova intermetallics ; atomic scale structure ; microstructure ; phase transitions ; transmission electron microscopy Vědní obor RIV BM - Fyzika pevných látek a magnetismus Obor OECD Condensed matter physics (including formerly solid state physics, supercond.) CEP EF16_019/0000760 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy LM2018110 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy GA19-09882S GA ČR - Grantová agentura ČR Způsob publikování Omezený přístup Institucionální podpora FZU-D - RVO:68378271 UT WOS 000833519500001 EID SCOPUS 85131395905 DOI 10.1016/j.matchar.2022.112007 Anotace Using common and high resolution transmission electron microscopy (TEM), we study the magnetic and crystal phase structures as well as their evolution in Ni50Mn25Ga20Fe5 magnetic shape memory material with high Curie point. The particular alloying by Fe and changing thickness of the TEM foil enable us to observe all martensitic phases known in Ni-Mn-Ga Heusler alloy system and their respective transitions simultaneously. Starting from cubic austenite at about 10 nm foil thickness, the structure evolves via peculiar interleaved stripes of austenite and five-layered modulated 10M martensite to pure 10M phase with a low density of stacking faults at 40 nm thickness. With further increasing thickness, the 10M phase transforms gradually to seven-layered modulated 14M martensite with an increased density of stacking faults. Finally, the non-modulated tetragonal NM phase appears within the 14M phase by detwinning of nanotwins forming the modulated phases.