Photoluminescence of Er/Yb-doped zinc-silicate glass and glass ceramics with ZnO and Zn2SiO4 nanoparticles
- 1.
SYSNO ASEP 0560330 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Photoluminescence of Er/Yb-doped zinc-silicate glass and glass ceramics with ZnO and Zn2SiO4 nanoparticles Tvůrce(i) Vařák, Petr (URE-Y)
Baborák, J. (CZ)
Cajzl, J. (CZ)
Nekvindová, P. (CZ)Celkový počet autorů 4 Číslo článku 1214213 Zdroj.dok. FIBER LASERS AND GLASS PHOTONICS: MATERIALS THROUGH APPLICATIONS III, 12142. - Bellingham : SPIE, 2022 / Ferrari M. ; Seddon A.B. ; Taccheo S. - ISSN 0277-786X - ISBN 978-1-5106-5160-9 Rozsah stran roč. 12142 (2022) Edice Proceedings of SPIE Poč.str. 6 s. Forma vydání Tištěná - P Akce Conference on Fiber Lasers and Glass Photonics - Materials through Applications III Part of SPIE Photonics Europe Conference Datum konání 03.04.2022 - 20.05.2022 Místo konání ELECTR NETWORK Země FR - Francie Typ akce WRD Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova Erbium ; glass ; glass-ceramics ; zinc ; silicate ; zinc oxide ; willemite Vědní obor RIV JA - Elektronika a optoelektronika, elektrotechnika Obor OECD Electrical and electronic engineering Institucionální podpora URE-Y - RVO:67985882 UT WOS 000838027400038 EID SCOPUS 85132848333 DOI 10.1117/12.2620488 Anotace Zinc-silicate glass-ceramic materials based on ZnO and Zn2SiO4 nanoparticles distributed in amorphous silica matrix represent one of the most perspective options to improve the photoluminescence properties of Er3+ ions, thanks to their low phonon energy and the possibility of energy transfer between the ZnO/Zn2SiO4 nanoparticles and Er3+ ions. In this paper, we focus on the investigation of crystallization in the sodium- and potassium-zinc-silicate system and the photoluminescence properties of Er3+-doped glass-ceramic materials. It was found that the presence of Na2O promotes the crystallization of Zn2SiO4 resulting in non-transparent glass-ceramic material at 750 degrees C, whereas the K2O-ZnO-SiO2 material remained transparent in the entire heat treatment range. Nevertheless, the crystallization of ZnO and Zn2SiO4 leads to an increase of photoluminescence intensity of Er3+ ions by up to 300 % compared to the pre-cursor glass. The Stark-splitting of the Er3+ emission spectra at 1.5 mu m after 978 nm excitation as well as shortening of the fluorescence lifetime suggest the incorporation of Er3+ ions inside the highly symmetric environment of ZnO and Zn2SiO4. Pracoviště Ústav fotoniky a elektroniky Kontakt Petr Vacek, vacek@ufe.cz, Tel.: 266 773 413, 266 773 438, 266 773 488 Rok sběru 2023 Elektronická adresa https://doi.org/10.1117/12.2620488
Počet záznamů: 1