B2 -> B19' ->B2(T) Martensitic Transformation as a Mechanism of Plastic Deformation of NiTi.
- 1.
SYSNO ASEP 0522366 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název B2 -> B19' ->B2(T) Martensitic Transformation as a Mechanism of Plastic Deformation of NiTi. Tvůrce(i) Šittner, Petr (UJF-V) ORCID, RID, SAI
Heller, Luděk (UJF-V) ORCID
Sedlák, Petr (UJF-V) ORCID
Kadeřávek, Lukáš (UJF-V) ORCID
Chen, Y. (CN)
Tyc, Ondřej (FZU-D) ORCID
Molnárová, Orsolya (FZU-D) ORCID
Seiner, Hanuš (UT-L) RID, ORCIDCelkový počet autorů 8 Zdroj.dok. Conference Proceedings from International Conference on Shape Memory and Superelastic Technologies, SMST 2019. - : ASM International Ohio : ASM International, 2019 - ISBN 978-151089272-9 Rozsah stran s. 167-168 Poč.str. 1 s. Forma vydání Tištěná - P Akce International Conference on Shape Memory and Superelastic Technologies 2019, SMST 2019 Datum konání 13.05.2019 - 17.05.2019 Místo konání Konstanz Země DE - Německo Typ akce WRD Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova materials ; stress-induced martensitic transformation ; twinning Vědní obor RIV BM - Fyzika pevných látek a magnetismus Obor OECD Condensed matter physics (including formerly solid state physics, supercond.) CEP EF16_013/0001794 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Institucionální podpora FZU-D - RVO:68378271 ; UJF-V - RVO:61389005 ; UT-L - RVO:61388998 EID SCOPUS 85077291101 Anotace Deformation of superelastic NiTi wire with tailored microstructure was investigated in tensile loading-unloading tests up to the end of the stress plateau in wide temperature range from room temperature up to 200 degrees C. Lattice defects left in the microstructure of deformed wires were investigated by transmission electron microscopy. Tensile deformation is localized up to the highest test temperatures, even if practically no martensite phase exists in the wire at the end of the stress plateau. In tensile tests at elevated temperatures around 100 degrees C, at which the upper plateau stress approaches the yield stress for plastic deformation of martensite, upper plateau strains become unusually long, transformation strains become unrecoverable and deformation bands containing {114} austenite twins appear in the microstructure of deformed wires. Pracoviště Ústav jaderné fyziky Kontakt Markéta Sommerová, sommerova@ujf.cas.cz, Tel.: 266 173 228 Rok sběru 2020
Počet záznamů: 1