Tm-doping concentration influence on Tm:GGAG lasing and tenability at 2 μm spectral region
- 1.
SYSNO ASEP 0521940 Druh ASEP A - Abstrakt Zařazení RIV Záznam nebyl označen do RIV Zařazení RIV Není vybrán druh dokumentu Název Tm-doping concentration influence on Tm:GGAG lasing and tenability at 2 μm spectral region Tvůrce(i) Kratochvíl, J. (CZ)
Boháček, P. (CZ)
Šulc, J. (CZ)
Němec, M. (CZ)
Fibrich, M. (CZ)
Jelínková, H. (CZ)
Trunda, Bohumil (FZU-D)
Havlák, Lubomír (FZU-D) RID, ORCID
Jurek, Karel (FZU-D) RID, ORCID, SAI
Nikl, Martin (FZU-D) RID, ORCID, SAICelkový počet autorů 10 Zdroj.dok. Proceedings of the European Conference on Lasers and Electro-Optics (CLEO 2019). - New York : IEEE, 2019 - ISBN 978-1-7281-0469-0
S. 46-46Poč.str. 1 s. Akce The European Conference on Lasers and Electro-Optics 2019 Datum konání 23.06.2019 - 27.06.2019 Místo konání Munich Země DE - Německo Typ akce WRD Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova gadolinium gallium aluminium garnet ; tunability parameters Vědní obor RIV BH - Optika, masery a lasery Obor OECD Optics (including laser optics and quantum optics) Institucionální podpora FZU-D - RVO:68378271 Anotace Tm3+ doped mixed gadolinium-gallium-aluminium-garnet (GGAG) is investigated. Focus is given to the Tm3+ concentration dependence of lasing and tunability parameters. The Tm:GGAG crystal was grown using Czochralski method in a slightly oxidative atmosphere. Five planeparallel face-polished Tm:GGAG samples with concentrations varying from 1.4 at.% to 8.4 at.% (Tm/Gd) and thicknesses ranging from 2.7 mm to 3.6 mm were cut from the crystal. The samples were longitudinally pumped by fiber coupled (core diam. 400 μm, NA = 0.22) laser diode at wavelength 785 nm in QCW regime (pulse length 5 ms, repetition rate 10 Hz). The 145 mm resonator consisted of a flat pumping mirror (HR @ 1.85–2.11 μm, HT @ 0.78 μm) and concave output coupler (r = 150 mm, R = 97.5 % @1.8 – 2.10 μm). For the wavelength tuning, 1.5 mm thick birefringent SiO2 plate was inserted in the cavity at the Brewster’s angle.
Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2020
Počet záznamů: 1