Silver-doped hydroxyapatite coatings deposited by suspension plasma spraying
- 1.
SYSNO ASEP 0498201 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Silver-doped hydroxyapatite coatings deposited by suspension plasma spraying Tvůrce(i) Čížek, Jan (UFP-V) ORCID
Brožek, Vlastimil (UFP-V) RID
Chráska, Tomáš (UFP-V) RID, ORCID
Lukáč, František (UFP-V) ORCID
Medřický, Jan (UFP-V) RID
Mušálek, Radek (UFP-V) RID, ORCID
Tesař, Tomáš (UFP-V) ORCID
Šiška, Filip (UFM-A) RID, ORCID
Antos, Z. (CZ)
Čupera, J. (CZ)
Matejková, M. (CZ)
Spotz, Z. (CZ)
Houdková, Š. (CZ)
Kverka, Miloslav (MBU-M) RID, ORCIDCelkový počet autorů 14 Zdroj.dok. Journal of Thermal Spray Technology. - : Springer - ISSN 1059-9630
Roč. 27, č. 8 (2018), s. 1333-1343Poč.str. 11 s. Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova antibacterial property ; HA ; hybrid water-stabilized plasma ; liquid feedstock ; Silver compounds Vědní obor RIV JK - Koroze a povrchové úpravy materiálů Obor OECD Coating and films Vědní obor RIV – spolupráce Ústav fyziky materiálu - Koroze a povrchové úpravy materiálů
Mikrobiologický ústav - Mikrobiologie, virologieCEP GB14-36566G GA ČR - Grantová agentura ČR Institucionální podpora UFP-V - RVO:61389021 ; UFM-A - RVO:68081723 ; MBU-M - RVO:61388971 UT WOS 000452893200009 EID SCOPUS 85055292484 DOI https://doi.org/10.1007/s11666-018-0767-2 Anotace Pure hydroxyapatite suspension was produced by wet chemical synthesis. Using a hybrid water-stabilized torch, a series of HA coatings were produced on SS304 and Ti6Al4V substrates and their properties were characterized by SEM, EDX and XRD techniques. After deposition, the amorphous phase content reached 6-10% and the coatings retained 75-82% of crystalline HA phase. Their thickness reached 145 μm. To understand the wear behavior of the coatings, pin-on-disc tribology evaluation was performed. Additionally, a set of HA coatings was prepared with pure metallic Ag content. This formed by in situ chemical decomposition of AgNO3 added into the HA suspension. The Ag was dispersed evenly within the coatings in the form of submicron-sized particles situated predominantly along the HA splats boundaries with a total Ag content of 8 wt.%. Given the antibacterial properties of Ag, such result presents a promising step forward in the hard tissue replacement research. Pracoviště Ústav fyziky plazmatu Kontakt Vladimíra Kebza, kebza@ipp.cas.cz, Tel.: 266 052 975 Rok sběru 2019 Elektronická adresa https://link.springer.com/article/10.1007/s11666-018-0767-2