Surface profile evolution and fatigue crack initiation in Sanicro 25 steel at room temperature
- 1.
SYSNO ASEP 0465502 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Surface profile evolution and fatigue crack initiation in Sanicro 25 steel at room temperature Tvůrce(i) Polák, Jaroslav (UFM-A) RID, ORCID
Petráš, Roman (UFM-A)
Chai, G. (SE)
Škorík, Viktor (UFM-A) RIDCelkový počet autorů 4 Zdroj.dok. Materials Science and Engineering A Structural Materials Properties Microstructure and Processing. - : Elsevier - ISSN 0921-5093
Roč. 658, MAR (2016), s. 221-228Poč.str. 8 s. Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova Sanicro 25 steel ; Fatigue crack initiation ; Persistent slip markings ; Extrusions ; Intrusions Vědní obor RIV JL - Únava materiálu a lomová mechanika CEP ED1.1.00/02.0068 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy EE2.3.30.0063 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy GA13-23652S GA ČR - Grantová agentura ČR Institucionální podpora UFM-A - RVO:68081723 UT WOS 000372560800025 EID SCOPUS 84957068456 DOI 10.1016/j.msea.2016.02.016 Anotace Evolution of the surface profile in room temperature cyclic loading has been studied in high alloy austenitic Sanicro 25 stainless steel. The localization of the cyclic plastic strain into persistent slip bands in the volume of the material leads to the formation of the specific surface relief in the form of persistent slip markings (PSMs) consisting of extrusions and intrusions. Evolution of the shape of PSMs was studied during interruption of cycling using SEM and FIB techniques. Three-dimensional information about the PSMs profiles was obtained. The profiles of both extrusions and intrusions and their evolution during cyclic loading were assessed. Generally extrusions grow, intrusions deepen and fatigue cracks initiate from the tip of the deepest intrusions. The experimental observations were compared and discussed in relation to existing physical models of surface relief formation and fatigue crack initiation. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2017
Počet záznamů: 1