Fatigue properties of nickel-base superalloy inconel 792-5A at 800°C
- 1.
SYSNO ASEP 0354177 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Fatigue properties of nickel-base superalloy inconel 792-5A at 800°C Tvůrce(i) Šmíd, Miroslav (UFM-A) RID, ORCID
Obrtlík, Karel (UFM-A) RID, ORCID
Petrenec, Martin (UFM-A)
Polák, Jaroslav (UFM-A) RID, ORCID
Hrbáček, K. (CZ)Zdroj.dok. Metal 2010 - 19th international conference on metallurgy and materials. - Ostrava : Tanger s.r.o, 2010 - ISBN 978-80-87294-15-4 Rozsah stran s. 1-6 Poč.str. 6 s. Forma vydání CD-ROM - CD-ROM Akce Metal 2010. International Conference on Metallurgy and Materials /19./ Datum konání 18.05.2010-20.05.2010 Místo konání Rožnov pod Radhoštěm Země CZ - Česká republika Typ akce EUR Jazyk dok. eng - angličtina Země vyd. CZ - Česká republika Klíč. slova Inconel 792-5A ; low cycle fatigue ; high temperatures ; fatigue life curves ; dislocation structure Vědní obor RIV JL - Únava materiálu a lomová mechanika CEP GA106/08/1631 GA ČR - Grantová agentura ČR CEZ AV0Z20410507 - UFM-A (2005-2011) Anotace Smooth specimens were cyclically strained under strain control with constant strain amplitude and constant strain rate. Low cycle fatigue tests were conducted in servo-hydraulic pulsator MTS equipped with a three zone resistance furnace at temperature 800°C in air. Fracture surface was studied in SEM after fatigue test termination. Selected specimens were used to prepare foils for the transmission electron microscope (TEM) observation of microstructure and dislocation arrangement. They were used to obtain cyclic hardening/softening curves, cyclic stress-strain curve and fatigue life curves in the representation of stress amplitude, total strain amplitude and plastic strain amplitude versus number of cycles to fracture. Experimental points can be approximated with the Manson-Coffin law and the Basquin law. Fracture surface examinations revealed fatigue crack initiation sites. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2011
Počet záznamů: 1