Formation of Layered Double Hydroxides on Alumina Surface in Aqueous Solutions Containing Divalent Metal Cations
- 1.
SYSNO ASEP 0333297 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Formation of Layered Double Hydroxides on Alumina Surface in Aqueous Solutions Containing Divalent Metal Cations Překlad názvu Tvorba LDH na povrchu aluminy v roztocích obsahujících divalentní kovové ionty Tvůrce(i) Kovanda, F. (CZ)
Mašátová, P. (CZ)
Novotná, P. (CZ)
Jirátová, Květa (UCHP-M) RID, ORCID, SAIZdroj.dok. Clays and Clay Minerals. - : Springer - ISSN 0009-8604
Roč. 57, č. 4 (2009), s. 425-432Poč.str. 8 s. Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova deposition ; layered double hydroxides ; supported mixed oxides Vědní obor RIV CI - Průmyslová chemie a chemické inženýrství CEP GA104/07/1400 GA ČR - Grantová agentura ČR CEZ AV0Z40720504 - UCHP-M (2005-2011) UT WOS 000271401600003 DOI 10.1346/CCMN.2009.0570403 Anotace A formation of layered double hydroxides (LDHs) on an Al2O3/Al support prepared by anodic oxidation of aluminum foil was studied in diluted aqueous solutions of Co, Mn, and/or Ni nitrates. The LDH deposition was carried out under hydrothermal conditions at 80 – 180 °C for time ranging from 8 to 168 hours. The LDH phase was formed after long-term deposition (3 – 7 days) at 120 – 160 °C and only a slight incorporation of Mn into the deposited LDHs was found. Ni cations when present in the solution were preferentially incorporated into the LDH phase; a homogeneous layer was formed, with single platy crystals oriented perpendicularly towards the support. After calcination at 500 °C, the products formed on Al2O3/Al support exhibited worse reducibility in comparison with mixed oxides obtained by thermal decomposition of coprecipitated LDHs. Pracoviště Ústav chemických procesů Kontakt Eva Jirsová, jirsova@icpf.cas.cz, Tel.: 220 390 227 Rok sběru 2010
Počet záznamů: 1