Crack initiation criteria for singular stress concentrations, Part IV: Applications to fracture of coated structures

  1. 1.
    SYSNO ASEP0322243
    Druh ASEPJ - Článek v odborném periodiku
    Zařazení RIVJ - Článek v odborném periodiku
    Poddruh JOstatní články
    NázevCrack initiation criteria for singular stress concentrations, Part IV: Applications to fracture of coated structures
    Překlad názvuKritéria iniciace trhlin ze singulárních koncentrátorů napětí. Část IV: Aplikace na povlakované konstrukce
    Tvůrce(i) Knésl, Zdeněk (UFM-A)
    Náhlík, Luboš (UFM-A) RID, ORCID
    Bareš, Pavel (UFM-A)
    Zdroj.dok.Engineering Mechanics. - : Association for Engineering Mechanics - ISSN 1802-1484
    Roč. 15, č. 4 (2008), s. 263-270
    Poč.str.8 s.
    Jazyk dok.eng - angličtina
    Země vyd.CZ - Česká republika
    Klíč. slovaFracture mechanics ; bi-material body ; thin layers ; fracture of coated structures
    Vědní obor RIVJL - Únava materiálu a lomová mechanika
    CEPGA106/07/1284 GA ČR - Grantová agentura ČR
    KJB200410803 GA AV ČR - Akademie věd
    CEZAV0Z20410507 - UFM-A (2005-2011)
    AnotaceThe influence of through crack in the protective surface layer on damage of coated structure is investigated. The coated structure is modeled as a particular case of a bi-material body consisting of thin surface layer on the substrate. Specific attention is devoted to the case of a through coating crack with its tip at the interface between coating and the substrate. To estimate how the coating crack with its tip at the interface influences the substrate failure the general approach described in [1,2,3] (Part I,II III of this contribution) is applied. An approximate approach based on calculations of crack mouth opening displacement for thin protective layers is suggested and developed. It is concluded that in the case of a stiffer coating on a more compliant substrate, the through coating cracks represent dangerous stress concentrators and, as a consequence of elastic mismatch of both materials, the critical applied stress for substrate failure decreases.
    PracovištěÚstav fyziky materiálu
    KontaktYvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485
    Rok sběru2009
Počet záznamů: 1  

  Tyto stránky využívají soubory cookies, které usnadňují jejich prohlížení. Další informace o tom jak používáme cookies.