Creep in copper dispersion strengthened with fine alumina particles and reinforced with alumina short fibres-in ODS copper matrix..
- 1.
SYSNO ASEP 0108210 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Ostatní články Název Creep in copper dispersion strengthened with fine alumina particles and reinforced with alumina short fibres-in ODS copper matrix.. Překlad názvu Creep mědi disperzně zpevněné jemnými částicemi a vyztužené krátkými vlákny oxidu hliníku v měděné matrici ODS Tvůrce(i) Čadek, Josef (UFM-A)
Kuchařová, Květa (UFM-A) RID, ORCID
Milička, Karel (UFM-A)Zdroj.dok. Journal of Alloys and Compounds. - : Elsevier - ISSN 0925-8388
Roč. 378, 1-2 (2004), s. 123-126Poč.str. 4 s. Akce International Symposium Physics of Materials /9./ Datum konání 01.09.2003-04.09.2003 Místo konání Prague Země CZ - Česká republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova Metals ; Powder metallurgy ; High temperature alloys Vědní obor RIV JI - Kompozitní materiály CEP IBS2041001 GA AV ČR - Akademie věd CEZ AV0Z2041904 - UFM-A Anotace Creep in copper dispersion strengthened with fine alumina particles and reinforced with alumina short fibres is investigated in two temperature intervals, namely lower temperature interval (LTI) 673-773 K and higher temperature interval (HTI) 923-1023 K. In both intervals, creep is associated with true threshold stresses decreasing with increasing temperature more strongly than the shear modulus of copper. The true threshold stress in the composite is higher than that in its matrix by a factor 2, by which the flow stress in the matrix is reduced due to load transfer. The creep strain rate is dislocation core diffusion controlled in LTI and lattice diffusion controlled in HTI. High values of the activation energies are explained in terms of the temperature dependence of the true threshold stress in LTI as well as in HTI. The high values of the stress exponents are explained in terms of the true threshold stresses. The true threshold stress is identified with the detachment stress Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2005
Počet záznamů: 1