0091055 - ÚFM 2008 CH eng A - Abstrakt
Kratochvíl, P. - Dobeš, Ferdinand - Milička, Karel - Pešička, J.
The Change of the Mechanical Properties and of the Structure of the Alloy during Gradual Approach of its Composition from Fe-40Al to Fe-43Al-4C (at. %).
[Změna mechanických vlastností a struktury slitiny během postupné změny složení od Fe-40Al na Fe-43Al-4C (at. %).]
Discussion Meeting on the Development of Innovative Iron Aluminium Alloys /4./. Duebendorf: EMPA - Materials Science and Technology, 2007 - (Palm, M.; Spiegel, M.; Stein, F.; Krein, R.). s. 42-42
[Discussion Meeting on the Development of Innovative Iron Aluminium Alloys /4./. 21.10.2007-24.10.2007, Interlaken]
Grant CEP: GA ČR GA106/05/0409; GA ČR GA106/06/0019
Výzkumný záměr: CEZ:AV0Z20410507
Klíčová slova: creep * iron aluminide (FeAl type) * heat-resistant alloy
Kód oboru RIV: JG - Hutnictví, kovové materiály

The mechanical properties were tested at 600 °C. Compression testing and creep tests in compression were performed with 8 alloys with different concentrations of carbon. The quantities describing the deformation process (flow stress, activation energy, stress exponent) are related to the phase and dislocation structure observed after the deformation tests. The effect of the presence of Si on the appearing of Al4C3 was observed.

Mechanické vlastnosti byly studovány při teplotě 600 °C. Zkoušky v jednoosém tlaku a creepové zkoušky byly provedeny na 8 slitinách s různým obsahem uhlíku. Veličiny popisující proces deformace (mez kluzu, aktivační energie, napěťový exponent) jsou vztaženy k fázové a dislokační struktuře pozorované po deformaci. Byl pozorován vliv křemíku na výskyt karbidu Al4C3.
Trvalý link: http://hdl.handle.net/11104/0151745