Effect of surface carbonitriding by plasma immersion ion implantation on the fatigue behaviour of 316L austenitic stainless stee
- 1.
SYSNO ASEP 0026256 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Effect of surface carbonitriding by plasma immersion ion implantation on the fatigue behaviour of 316L austenitic stainless stee Překlad názvu Vliv povrchové karbonitridace plazmovou imerzní iontovou implantací na únavové chování austenitické nerezavějící oceli 316L Tvůrce(i) Obrtlík, Karel (UFM-A) RID, ORCID
Jirásková, Yvonna (UFM-A) RID, ORCID
Man, Jiří (UFM-A) RID, ORCID
Polák, Jaroslav (UFM-A) RID, ORCIDZdroj.dok. Computer Methods and Experimental Measurements for Surface Effects and Contact Mechanics /7./. - Southampton : WIT Press, 2005 / De Hosson J.T.M. ; Brebia C.A. ; Nishida S.I. - ISBN 1-84564-022-5 Rozsah stran s. 13-22 Poč.str. 10 s. Akce Contact Surface 2005 /7./ Datum konání 05.09.2005-07.09.2005 Místo konání Bologna Země IT - Itálie Typ akce WRD Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova austenitic stainless steel ; fatigue life curves ; plasma immersion ion implantation Vědní obor RIV JL - Únava materiálu a lomová mechanika CEP GA106/03/1265 GA ČR - Grantová agentura ČR 1QS200410502 GA AV ČR - Akademie věd ME 373 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy CEZ AV0Z20410507 - UFM-A (2005-2011) Anotace Cylindrical specimens of 316L austenitic stainless steel in as-received condition and with surface carbonitriding by plasma immersion ion implantation were cyclically strained under plastic strain control. Micro-hardness depth profile of hardened surface layer was measured. Mössbauer spectroscopy and X-ray diffraction were used to study the phase composition of the treated layer. Stress-strain response and fatigue life data of both materials were obtained. Surface relief and fracture surface were examined to study fatigue damage mechanisms. Two domains separated by the transitional plastic strain amplitude could be distinguished in fatigue behaviour of the treated steel. In the low amplitude domain, the main crack originates in subsurface region resulting in the prolonged lifetime. The main crack initiates at the surface in the high amplitude domain and the fatigue life of the treated steel is reduced compared to the untreated one. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2006
Počet záznamů: 1