Co‐implantation of Er and Yb ions into single‐crystalline and nano‐crystalline diamond

0500971 - ÚFE 2019 RIV GB eng J - Článek v odborném periodiku
Cajzl, Jakub - Akhetova, B. - Nekvindová, P. - Macková, Anna - Malinský, Petr - Oswald, Jiří - Remeš, Zdeněk - Varga, Marián - Kromka, Alexander
Co‐implantation of Er and Yb ions into single‐crystalline and nano‐crystalline diamond.
Surface and Interface Analysis. Roč. 50, č. 11 (2018), s. 1218-1223. ISSN 0142-2421. E-ISSN 1096-9918.
[17th European Conference on Applications of Surface and Interface Analysis (ECASIA 2017). Monpellier, 24.09.2017-29.09.2017]
Grant CEP: GA MŠMT LM2015056; GA ČR GA15-01602S; GA MŠMT(CZ) LTC17029
Institucionální podpora: RVO:67985882 ; RVO:61389005 ; RVO:68378271
Klíčová slova: nano-crystalline diamond * diamond * erbium * ytterbium
Obor OECD: Condensed matter physics (including formerly solid state physics, supercond.); Nuclear physics (UJF-V); Optics (including laser optics and quantum optics) (FZU-D)
Impakt faktor: 1.319, rok: 2018

The paper reports on the results of Er-Yb and Er-Al co-implantation into commercial single-crystalline diamonds as well as into nano-crystalline diamond (NCD) thin films and their photoluminescence properties. The NCD thin films were deposited on fused silica glass by linear-antenna microwave plasma-enhanced chemical vapour deposition (PE MWCVD). Er implantation was performed at an energy of 190 keV and fluences of 1 x 10(15) and 5 x 10(15) ions. cm(-2) followed by Yb co-implantation under the same conditions or Al co-implantation at an energy of 40 keV and the same fluences. The concentration depth profiles of the elements and the degree of their crystal damage (structural ordering) were measured using Rutherford backscattering spectroscopy and Rutherford backscattering spectroscopy/channelling, respectively. Structural changes were studied by Raman spectroscopy. All Er-Yb doped samples revealed measurable photoluminescence at approximately 1.5 mu m. A comparison with Er-implanted samples showed that the Er-Yb co-implantation was beneficial for the photoluminescence at 1.5 mu m in both substrates. Er-doped NCD films revealed higher intensity of luminescence than Er-doped single-crystal diamond. This observation is attributed to the specific incorporation of Er into the diamond and at the grain boundaries