High-cycle fatigue of IN 713LC

0322739 - ÚFM 2009 RIV CZ eng C - Konferenční příspěvek (zahraniční konf.)
Kunz, Ludvík - Lukáš, Petr - Mintách, Rastislav - Konečná, R.
High-cycle fatigue of IN 713LC.
[Vysokocyklová únava IN 713LC.]
Proceedings of 17th European Conference on Fracture. Brno: VUTIUM Brno, 2008 - (Pokluda, J.; Lukáš, P.; Šandera, P.; Dlouhý, I.), s. 945-951. ISBN 978-80-214-3692-3.
[ECF17 - European Conference on Fracture /17./. Brno (CZ), 02.09.2008-05.09.2008]
Grant CEP: GA MPO FT-TA4/023
Výzkumný záměr: CEZ:AV0Z20410507
Klíčová slova: Inconel 713LC * high cycle fatigue * casting defects * largest extreme value statistic
Kód oboru RIV: JG - Hutnictví, kovové materiály

High-cycle fatigue strength of Ni-base superalloy IN 713LC was experimentally determined for symmetrical loading and for loading with tensile mean stresses at a temperature of 800 °C in air. An analysis of the influence of microstructure on fatigue crack initiation and related fatigue strength was performed. Statistical method of the largest extreme value has been applied to characterize the casting defect distribution.

Experimentálně byla stanovena vysokocyklová únavová pevnost niklové superslitiny IN 713LC pro symetrický zatěžovací cyklus a pro zatěžování s tahovým středním napětím. Zkoušky byly provedeny při teplotě 800 °C na vzduchu. Byla provedena analýza vlivu mikrostruktury únavovou pevnost a na iniciaci únavových trhlin. Pro charakterizaci distribuce licích defektů byla použita statistická metoda rozdělení extrémních hodnot.