Epitaxial growth of thin films of X-type Sr2Co2Fe28O46 hexaferrite by chemical solution deposition
- 1.0574981 - ÚACH 2024 RIV NL eng J - Článek v odborném periodiku
Soroka, Miroslav - Buršík, Josef - Kužel, R. - Horák, L. - Prokleška, J. - Vronka, M. - Laguta, V.
Epitaxial growth of thin films of X-type Sr2Co2Fe28O46 hexaferrite by chemical solution deposition.
Journal of the European Ceramic Society. Roč. 43, č. 15 (2023), s. 6916-6924. ISSN 0955-2219. E-ISSN 1873-619X
Grant CEP: GA ČR(CZ) GA19-06433S; GA MŠMT(CZ) LM2018124
Výzkumná infrastruktura: CzechNanoLab II - 90251
Institucionální podpora: RVO:61388980
Klíčová slova: Chemical solution deposition * Spin reorientation transition * Thin films * X-type hexaferrites * Sr2Co2Fe28O46
Obor OECD: Inorganic and nuclear chemistry
Impakt faktor: 5.7, rok: 2022
Způsob publikování: Omezený přístup
https://doi.org/10.1016/j.jeurceramsoc.2023.07.027
Although single crystals of hexaferrites have received considerable attention, the same does not apply for thin films. Here, the growth of epitaxial thin films of Sr2Co2Fe28O46 on a SrTiO3(111) by a chemical solution deposition method is reported. Using X-ray diffraction analysis, the orientation relationship between film and substrate was established as (000l)X || (111)STO and 112̅0X || 101̅STO. The magnetization and magnetic domain structure were investigated using magnetic measurements and Lorentz transmission electron microscopy, respectively. With changing temperature, the magnitude of magnetization in the (0001) plane changed at ∼355 K, while that along the [0001] direction remained almost unchanged, suggesting a spin reorientation transition. Using the ferromagnetic resonance method, it was shown that the compound exhibits a change in the orientation of the magnetic anisotropy in the (0001) plane at ∼ 150 K that supports the occurrence of the multiaxial anisotropy state in film similar to that in single crystals.