Optimization of wear-, fracture- and corrosion performance of Vanadis 6 steel through cryogenic treatment and tempering

0573947 - ÚFM 2025 RIV GB eng C - Konferenční příspěvek (zahraniční konf.)
Jurči, P. - Yarasu, V. - Dlouhý, Ivo - Bartkowska, A.
Optimization of wear-, fracture- and corrosion performance of Vanadis 6 steel through cryogenic treatment and tempering.
IOP Conference Series-Materials Science and Engineering. Vol. 1284. Bristol: IOP Publishing, 2023 - (Asnafi, N.; Lindgren, L.), s. 012086. ISSN 1757-8981.
[IDDRG - Conference of the International-Deep-Drawing-Research-Group /42./. Lulea (SE), 19.06.2023-22.06.2023]
Institucionální podpora: RVO:68081723
Klíčová slova: cryogenic treatment * ledeburitic steel * fracture
Obor OECD: Materials engineering

Vanadis 6 cold work tool steel was vacuum austenitized, room temperature quenched, differently cryogenically treated (-75, -140 and -196 degrees C for different durations) and double tempered, at temperatures of either 170 or 530 degrees C. Galling resistance was assessed by pin-on-disc testing of differently treated specimens against CuSn bronze, at wide ranges of sliding velocities and loads. The obtained results show that cryogenic treatments combined with low temperature tempering improves anti-galling performance of the steel. The best tribological properties were obtained when high-temperature tempering was combined with cryogenic treatment at -196 degrees C, due to the maximum extent of microstructural alteration generated by this kind of treatment. The improvement in wear performance is accompanied with slight but undisputable increase in corrosion resistance of the steel, at almost no affected toughness as compared with the state after conventional heat treatment. In conclusion, the obtained results imply an opportunity to simultaneously improve wear performance, corrosion resistance and toughness of the examined steel, by choosing a proper combination of cryogenic treatment and tempering.