Fast continuous in-situ XCT of additively manufactured carbon fiber reinforced tensile test specimens

0572542 - ÚTAM 2024 RIV CZ eng C - Konferenční příspěvek (zahraniční konf.)
Glinz, J. - Maurer, J. - Holzleitner, M. - Pace, F. - Stamopoulos, A. - Vopálenský, Michal - Kumpová, Ivana - Eckl, M. - Kastner, J. - Senck, S.
Fast continuous in-situ XCT of additively manufactured carbon fiber reinforced tensile test specimens.
Acta Polytechnica CTU Proceedings. Vol. 42. Prague: Czech Technical University in Prague, 2023 - (Kytýř, D.; Doktor, T.; Zlámal, P.), s. 22-26. E-ISSN 2336-5382.
[Youth Symposium on Experimental Solid Mechanics /18./. Telč (CZ), 11.06.2023-14.06.2023]
Institucionální podpora: RVO:68378297
Klíčová slova: additive manufacturing * composites * X-ray computed tomography * in-situ tensile testing
Obor OECD: Materials engineering
https://doi.org/10.14311/APP.2023.42.0022

The reinforcement of fused filament fabricated (FFF) components with continuous fibers allows for high versatility in the design of mechanical properties for a specific application’s needs. However, the bonding quality between continuous fibers and the FFF matrix material has high impact on the overall performance of the composite. In a recent study [1], additively manufactured (AM) continuous fiber reinforced tensile test specimens have been investigated regarding the effect of amount and material of the embedded continuous fibers on tensile strength and AM build quality. During these tensile tests, a sudden reduction in tensile stress, which most likely was not related to actual rupture of continuous fibers, was noticeable. Since X-ray computed tomography (XCT) scans were performed only prior to and after the tensile testing, a detailed investigation on the origin of these drops in tensile stress was not possible. Within this work, we will expand upon these findings and present results of fast on-the-fly in-situ investigations performed on continuous carbon fiber reinforced specimens of the same AM build. During these investigations, specimens are loaded under the same conditions while fast XCT scans, with a total scan time of 12 seconds each, were performed consecutively. The resulting three-dimensional image data reveals internal meso- and macro-structural changes over time/strain to find the cause of the aforementioned reduction in tensile stress.
Trvalý link: https://hdl.handle.net/11104/0343917