Development of Energy-Efficient ”Cold” Curing Method for Polypropylene Glycol Fumarate Using an Optimized Initiating System

0570765 - ÚACH 2024 RIV KZ eng J - Článek v odborném periodiku
Burkeyeva, G. K. - Kovaleva, A. K. - Tazhbayev, Y. M. - Ibrayeva, Z. M. - Plocek, Jiří
Development of Energy-Efficient ”Cold” Curing Method for Polypropylene Glycol Fumarate Using an Optimized Initiating System.
Eurasian Journal of Chemistry. Roč. 109, č. 1 (2023), s. 68-77. ISSN 2959-0663. E-ISSN 2959-0671
Institucionální podpora: RVO:61388980
Klíčová slova: sealant * unsaturated polyester * polypropylene glycol fumarate * unsaturated carboxylic acid * methacrylic acid * radical copolymerization * ?cold? curing * initiating system
Obor OECD: Inorganic and nuclear chemistry
Způsob publikování: Open access

The possibility of using the polymeric matrix obtained as a result of “cold” polymerization of polypropylene glycol fumarate (p-PGF) with methacrylic acid (MAA) as a polymeric base for obtaining new adhesives of domestic production was demonstrated. The starting reagent (p-PGF) was synthesized by condensation polymerization of fumaric acid with propylene glycol in the presence of a catalyst, which reduced the temperature and shortened the process time. A number of solutions of p-PGF in MAA of different mass compositions were obtained and their rheological properties were determined. Curing of the studied solutions was carried out by radical polymerization at room temperature in the presence of the “cold curing” initiating system. The optimum composition and amount of components of the “cold” curing initiating system consisting of an initiator (benzoyl peroxide) and a promoter (dimethylaniline) were established. Technological parameters of curing (temperature, lifetime and curing time, the value of volume shrinkage) were determined. The obtained compounds were identified by infrared spectroscopy. The surface morphology of the cured samples was studied by scanning electron microscopy. It was found that varying the composition of the initial polymermonomer mixture allows controlling the physicochemical properties.