Mechanisms of intergranular fatigue crack initiation in polycrystalline materials

0570432 - ÚFM 2025 RIV NL eng C - Konferenční příspěvek (zahraniční konf.)
Polák, Jaroslav - Chlupová, Alice
Mechanisms of intergranular fatigue crack initiation in polycrystalline materials.
Procedia Structural Integrity. Vol. 43. Amsterdam: Elsevier B. V., 2023 - (Pokluda, J.; Šandera, P.), s. 197-202. ISSN 2452-3216.
[MSMF10 - International Conference on Materials Structure and Micromechanics of Fracture /10./. Brno (CZ), 12.09.2022-14.09.2022]
Institucionální podpora: RVO:68081723
Klíčová slova: fatigue crack * intergranular initiation * extrusions * intrusions * grain boundary damage
Obor OECD: Materials engineering

Fatigue failure in polycrystalline materials occurs by initiation and propagation of fatigue cracks. Fatigue cracks can initiate transgranularly or intergranularly. While considerable progress has been achieved in the explanation of the mechanism of transgranular fatigue crack initiation intergranular initiation is still the subject of controversy. A recent study of the crack initiation in superaustenitic Sanicro 25 steel [1] revealed the important role of persistent slip markings (PSMs) in the grains adjoining the grain boundary. A novel mechanism of intergranular fatigue crack initiation has been proposed. Provided the cyclic slip cannot proceed from one grain to the neighbour one, extrusions and intrusions arise not only on the surface but also on the grain boundary. Growing intrusions represent void-like defects and growing intrusions push neighbour grain apart. A systematic study of intergranular cracking has been performed on polycrystalline copper cycled with high and low strain amplitudes. SEM observations of the early stages of fatigue crack initiation on the grain boundaries, EBSD study of grains orientation, FIB cutting of the grain boundaries and simultaneous documentation of the effect of extrusions and intrusions on the grain boundary cohesion are reported simultaneously with the conditions favourable for the initiation of the fatigue cracks.