Fatigue behavior of DIN 1.4307 and DIN 1.4306 stainless steels under high frequency loading
- 1.0567149 - ÚFM 2025 RIV NL eng C - Konferenční příspěvek (zahraniční konf.)
Klusák, Jan - Kozáková, Kamila - Jambor, Michal - Seitl, Stanislav
Fatigue behavior of DIN 1.4307 and DIN 1.4306 stainless steels under high frequency loading.
Procedia Structural Integrity. Vol. 43. Amsterdam: Elsevier B. V., 2023 - (Pokluda, J.; Šandera, P.), s. 142-147. ISSN 2452-3216.
[MSMF10 - International Conference on Materials Structure and Micromechanics of Fracture /10./. Brno (CZ), 12.09.2022-14.09.2022]
Grant CEP: GA ČR(CZ) GA20-00761S
Institucionální podpora: RVO:68081723
Klíčová slova: Fatigue crack * stainless steel * ultrasonic frequency loading
Obor OECD: Materials engineering
Two stainless steels DIN 1.4307 and DIN 1.4306 were tested by an ultrasonic fatigue loading device under push-pull mode (stress ratio R = -1). Life-time curves were determined in the high and very high cycle fatigue regions. The time dependence of frequency was monitored and evaluated. At the beginning of the tests (up to 1 × 10^7 cycles), an increase of the frequency was observed, followed by a slow frequency decrease. It relates to changes of microstructure. No failure occurred in the region between 1 × 10^9 and 1 × 10^10 cycles. The steel 1.4306 exhibits a higher fatigue life-time than the steel 1.4307. This is caused by the difference in the chemical composition of the two steels, namely by the higher nickel content in the 1.4306 steel.