Amorphous Phase Formation and Heat Treating Evolution in Mechanically Alloyed Ti-Cu Alloy for Biomedical Applications

0564097 - ÚFM 2023 RIV IN eng J - Článek v odborném periodiku
Urban, P. - Astacio, R. - Ternero, F. - Náhlík, Luboš - Cintas, J.
Amorphous Phase Formation and Heat Treating Evolution in Mechanically Alloyed Ti-Cu Alloy for Biomedical Applications.
Transactions of The Indian Institute of Metals. Roč. 75, č. 12 (2022), s. 3039-3046. ISSN 0972-2815. E-ISSN 0975-1645
Institucionální podpora: RVO:68081723
Klíčová slova: Amorphization * Crystallization * Mechanical alloying * Titanium * Copper
Obor OECD: Materials engineering
Impakt faktor: 1.6, rok: 2022
Způsob publikování: Open access
https://link.springer.com/article/10.1007/s12666-022-02697-0

The present work aims to produce TixCu100-x (x = 90, 80, 70, and 60) amorphous alloys by using high energy ball mill. The microstructure and possible formation of amorphous phases were characterized employing laser granulometry, scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray diffraction (XRD). The amorphous-crystalline transformation at high temperatures was studied according to differential scanning calorimetry (DSC) and XRD. The Ti80Cu20 alloys were obtained in an amorphous state after 30 h of mechanical alloying, and the amorphous phase is stable up to 340 degrees C. At higher temperatures, this alloy crystallizes, forming the intermetallic compound Ti2Cu, and a substitutional solid solution Ti(Cu).