W plus Cu and W plus Ni Composites and FGMs Prepared by Plasma Transferred Arc Cladding

0555697 - ÚFP 2022 RIV CH eng J - Článek v odborném periodiku
Matějíček, Jiří - Antoš, J. - Rohan, P.
W plus Cu and W plus Ni Composites and FGMs Prepared by Plasma Transferred Arc Cladding.
Materials. Roč. 14, č. 4 (2021), č. článku 789. E-ISSN 1996-1944
Grant CEP: GA ČR(CZ) GA17-23154S
Grant ostatní: AV ČR(CZ) StrategieAV21/5
Program: StrategieAV
Institucionální podpora: RVO:61389021
Klíčová slova: plasma-facing materials * W-based composites * PTA cladding
Obor OECD: Materials engineering
Impakt faktor: 3.748, rok: 2021
Způsob publikování: Open access
https://www.mdpi.com/1996-1944/14/4/789

Tungsten-based materials are the most prospective candidates for plasma-facing components of future fusion devices, such as DEMO. W-based composites and graded layers can serve as stress-relieving interlayers for the joints between plasma-facing armor and the cooling or structural parts. Coating/cladding techniques offer the advantages of eliminating the joining step and the ability to coat large areas, even on nonplanar shapes. In this work, W + Cu and W + Ni composites were prepared by pulsed plasma transferred arc (PTA) cladding on several different substrates. Optimization of the process was carried out with respect to powder mixture composition and process parameters like arc current, plasma gas composition, and traverse velocity. Dense claddings of several millimeters thickness and various W content were achieved. Moreover, multilayers with W content gradually varying from 47 to 92% were formed. The structure, compositional profiles, and thermal properties of the claddings were characterized.