Electrical and Dielectric Properties of Sb2O3-PbCl2-AgCl Glass System

  1. 1.
    0546025 - ÚSMH 2022 RIV US eng J - Článek v odborném periodiku
    Bošák, O. - Kubliha, M. - Kostka, Petr - Minárik, S. - Dománková, M. - Le Coq, D.
    Electrical and Dielectric Properties of Sb2O3-PbCl2-AgCl Glass System.
    Russian Journal of Electrochemistry. Roč. 57, č. 7 (2021), s. 681-687. ISSN 1023-1935. E-ISSN 1608-3342
    Grant CEP: GA ČR(CZ) GA19-07456S; GA MŠMT(CZ) 8X20053
    Institucionální podpora: RVO:67985891
    Klíčová slova: antimony oxide-based glasses * electrical conductivity * ionic conductivity * complex electrical modulus
    Obor OECD: Ceramics
    Impakt faktor: 1.351, rok: 2021
    Způsob publikování: Omezený přístup
    https://link-springer-com.ezproxy.lib.cas.cz/article/10.1134%2FS1023193521070041

    Electrical and dielectric properties of ternary glasses in the Sb2O3-PbCl2-AgCl system were investigated across a broad temperature and frequency range. The studied glass system is interesting since it possesses a high ionic conductivity. The (Sb2O3)(x)-(PbCl2)(100y)(-)(x)-(AgCl)(y) glasses were prepared by melt-quenching method from high purity components. Different batches of these glasses were investigated with varying molar content of both Sb2O3 (45 <= x <= 70 mol %) and AgCl (5 <= y <= 25 mol %). The colour of the prepared chloro-antimonite glasses varies between yellow and brown. The glass transition temperature (T-g) decreases with increasing AgCl concentrations. DC and AC electrical conductivities and complex electrical modulus were measured across a temperature range from room temperature up to 200 degrees C and across a frequency range between 0.2 and 10(5) Hz. The dependence of DC conductivity on temperature follows the so-called Arrhenius-like equation. The DC conductivity at constant temperature significantly increases with increasing AgCl or PbCl2 content. It was found that the activation energy of conduction process decreases with the substitution of PbCl2 by AgCl from 1 eV down to 0.56 eV for (Sb2O3)(50)-(PbCl2)(45)-(AgCl)(5) and (Sb2O3)(50)-(PbCl2)(25)-(AgCl)(25), respectively. The influence of the composition on the AC conductivity of the investigated glasses is also discussed.