The temperature effect on the plastic deformation of the Mg88Zn7Y5 alloy with LPSO phase studied by in-situ synchrotron radiation diffraction

0545943 - ÚJF 2022 RIV GB eng J - Článek v odborném periodiku
Fekete, K. - Farkas, Gergely - Drozdenko, D. - Tolnai, D. - Stark, A. - Dobroň, P. - Garces, G. - Máthis, K.
The temperature effect on the plastic deformation of the Mg88Zn7Y5 alloy with LPSO phase studied by in-situ synchrotron radiation diffraction.
Intermetallics. Roč. 138, NOV (2021), č. článku 107321. ISSN 0966-9795. E-ISSN 1879-0216
Grant CEP: GA MŠMT EF16_013/0001794; GA MŠMT LM2018111
Institucionální podpora: RVO:61389005
Klíčová slova: LPSO phase * compression * kinking * elevated temperature * Synchrotron radiation diffraction
Obor OECD: Materials engineering
Impakt faktor: 4.075, rok: 2021
Způsob publikování: Omezený přístup
https://doi.org/10.1016/j.intermet.2021.107321

The temperature dependence of the compressive deformation behavior of the Mg88Zn7Y5 alloy with a high volume fraction (similar to 85%) of the long-period stacking-ordered (LPSO) phase was studied by in-situ synchrotron radiation diffraction. The as-extruded microstructure exhibits a fully recrystallized alpha-Mg phase with a nearly random texture. The LPSO phase, identified as the 18R polytype, is represented by wavy lamellae elongated along the extrusion direction and has an intensive basal texture. The alloy compressed along the extrusion direction at room temperature shows a superior yield strength of 480 MPa. With increasing deformation temperature, the yield strength is reduced by 15% at 200 degrees C and by 46% at 300 degrees C, respectively. At all tested temperatures, the basal slip is activated in the alpha-Mg matrix far below the yield strength. The macroscopic yielding of the alloy is controlled by the activation of deformation kinking in the LPSO phase. The synchrotron radiation diffraction data indicate the stress localization at kinks with respect to the grains having the same orientation.