A Raman spectroscopic analysis of polymer membranes with graphene oxide and reduced graphene oxide

0540228 - ÚMCH 2022 RIV CH eng J - Článek v odborném periodiku
Kolodziej, A. - Dlugoń, E. - Swietek, Malgorzata Anna - Ziabka, M. - Dawiec, E. - Gubernat, M. - Michalec, M. - Weselucha-Birczynska, A.
A Raman spectroscopic analysis of polymer membranes with graphene oxide and reduced graphene oxide.
Journal of Composites Science. Roč. 5, č. 1 (2021), č. článku 20. ISSN 2504-477X
Grant CEP: GA ČR(CZ) GA20-07015S
Institucionální podpora: RVO:61389013
Klíčová slova: polymer nanocomposite * poly(ε-caprolactone) * reduced graphene oxide (rGO)
Obor OECD: Polymer science
Způsob publikování: Open access
https://www.mdpi.com/2504-477X/5/1/20

Nowadays, despite significant advances in the field of biomaterials for tissue engineering applications, novel bone substituents still need refinement so they can be successfully implemented into the medical treatment of bone fractures. Generally, a scaffold made of synthetic polymer blended with nanofillers was proven to be a very promising biomaterial for tissue engineering, however the choice of components for the said scaffold remains questionable. The objects of the presented study were novel composites consisting of poly(ε-caprolactone) (PCL) and two types of graphene materials: graphene oxide (GO) and partially reduced graphene oxide (rGO). The technique of choice, that was used to characterize the obtained composites, was Raman micro-spectroscopy. It revealed that the composite PCL/GO differs substantially from the PCL/rGO composite. The incorporation of the GO particles into the polymer influenced the structure organisation of the polymeric matrix more significantly than rGO. The crystallinity parameters confirmed that the level of crystallinity is generally higher in the PCL/GO membrane in comparison to PCL/rGO (and even in raw PCL) that leads to the conclusion that the GO acts as a nucleation agent enhancing the crystallization of PCL. Interestingly, the characteristics of the studied nanofillers, for example: the level of the organisation (D/G ratio) and the in-plane size of the nano-crystallites (La) almost do not differ. However, they have an ability to influence polymeric matrix differently.