An ultrasonic study of relaxation processes in pure and mechanically alloyed tungsten
- 1.0537989 - ÚT 2021 RIV GB eng J - Článek v odborném periodiku
Koller, Martin - Vilémová, Monika - Lukáč, František - Beran, Přemysl - Čížek, B. - Hadraba, Hynek - Matějíček, Jiří - Veverka, Jakub - Seiner, H.
An ultrasonic study of relaxation processes in pure and mechanically alloyed tungsten.
International Journal of Refractory Metals & Hard Materials. Roč. 90, August (2020), č. článku 105233. ISSN 0263-4368. E-ISSN 2213-3917
Grant CEP: GA MŠMT EF16_019/0000778; GA MŠMT LM2015056
Výzkumná infrastruktura: Reactors LVR-15 and LR-0 II - 90120
Institucionální podpora: RVO:61388998 ; RVO:61389021 ; RVO:68081723 ; RVO:61389005
Klíčová slova: fine-grained tungsten * oxide dispersion * resonant ultrasound spectroscopy * ductile-to-brittle transition temperature * internal friction * dislocation density
Obor OECD: Acoustics; Materials engineering (UFP-V); Condensed matter physics (including formerly solid state physics, supercond.) (UJF-V); Materials engineering (UFM-A)
Impakt faktor: 3.871, rok: 2020
Způsob publikování: Omezený přístup
https://www.sciencedirect.com/science/article/abs/pii/S0263436820301098
High-temperature internal friction in a pure tungsten single crystal, polycrystals with different grain sizes, and mechanically alloyed tungsten polycrystals was studied. Positron annihilation spectroscopy was used to prove that all studied materials contain a detectable amount of dislocations. Then, resonant ultrasound spectroscopy was applied to determine the internal friction evolution with temperature from room temperature up to 740 degrees C. For the pure tungsten samples, a sharp increase of internal friction was observed for temperatures above 470 degrees C (for the single crystal) or above 400 degrees C (for the polycrystals), the activation energy corresponding to this increase was the same as the activation energy for the ductile-to-brittle transition in tungsten reported in the literature. For the alloyed materials, direct observation of the onset of this relaxation mechanism was impossible due to additional effects resulting from the secondary phases in the material.
Trvalý link: http://hdl.handle.net/11104/0316566