Ni-mediated reactions in nanocrystalline diamond on Si substrates: the role of the oxide barrier.
RSC Advances. Roč. 10, č. 14 (2020), s. 8224-8232. ISSN 2046-2069. E-ISSN 2046-2069
Grant CEP: GA MŠMT(CZ) EF16_019/0000760
Grant ostatní: OP VVV - SOLID21(XE) CZ.02.1.01/0.0/0.0/16_019/0000760
Institucionální podpora: RVO:68378271
Klíčová slova: oxide barrier * Si substrates * nanocrystalline diamond
Obor OECD: Condensed matter physics (including formerly solid state physics, supercond.)
Impakt faktor: 3.361, rok: 2020 ; AIS: 0.525, rok: 2020
Způsob publikování: Open access
DOI: https://doi.org/10.1039/d0ra00809e

Manocrystalline diamond (NCD)films grown on Si substrates by microwave plasma enhanced chemicalvapor deposition (MWPECVD) were subjected to Ni-mediated graphitization to cover them witha conductive layer. Results of transmission electron microscopy including electron energy-lossspectroscopy of cross-sectional samples demonstrate that the oxide layer on Si substrates ( 5 nm nativeSiO2) has been damaged by microwave plasma during the early stage of NCD growth. During the heattreatment for graphitizing the NCD layer, the permeability or absence of the oxide barrier allow Ninanoparticles to diffuse into the Si substrate and cause additional solid-state reactions producingpyramidal crystals of NiSi2and SiC nanocrystals. The latter are found impinged into the NiSi2pyramidsbut only when the interfacial oxide layer is absent, replaced by amorphous SiC. The complex phasemorphology of the samples is also reflected in the temperature dependence of electrical conductivity,where multiple pathways of the electronic transport dominate in different temperature regions. Wepresent models explaining the observed cascade of solid-state reactions and resulting electronictransport properties of such heterostructures.