Effect of magnetite transformations on degradation efficiency of cerium dioxide-magnetite composite.

0524979 - ÚFM 2021 RIV NL eng J - Článek v odborném periodiku
Jirásková, Yvonna - Buršík, Jiří - Ederer, J. - Janos, P. - Juřica, J. - Luňáček, J. - Životský, O.
Effect of magnetite transformations on degradation efficiency of cerium dioxide-magnetite composite.
Journal of Materials Research and Technology-JMR&T. Roč. 9, č. 3 (2020), s. 4431-4439. ISSN 2238-7854. E-ISSN 2214-0697
Grant CEP: GA MŠMT(CZ) LQ1601; GA MŠMT(CZ) EF17_048/0007399
Institucionální podpora: RVO:68081723
Klíčová slova: CeO2 * Iron Oxide * Microstructure * Magnetic properties * Mössbauer spectroscopy * Degradation efficiecy
Obor OECD: Environmental sciences (social aspects to be 5.7)
Impakt faktor: 5.039, rok: 2020
Způsob publikování: Open access
https://www.sciencedirect.com/science/article/pii/S2238785419322161?via%3Dihub

Present investigations are focused on synthesis of magnetite/cerium dioxide reactive sor-bents in various weight ratios of components and their characterization of chemical andmagnetic properties. The morphology and changes in magnetic transformations in depen-dence on composition are followed by electron microscopy, X-ray diffraction, Mössbauerspectroscopy and magnetic measurements at room and low temperatures. Degradationefficiency is evaluated from a decomposition of the organophosphorus pesticide parathionmethyl using prepared reactive sorbents. The experimental results reveal that the degra-dation efficiency, expressed by rate constant (mol/h) in dependence on amount of ceriumdioxide content (vol.%), is independent on kind of iron oxide but increases with cerium diox-ide content. On the contrary, saturation and remanent magnetizations are highly sensitiveto relative ratio of iron oxides, magnetite, maghemite and hematite, originating from theinitial magnetite transformations in dependence on sample composition.