Continuous-wave Tm:YAlO.sub.3./sub. laser at similar to 2.3 mu m
- 1.0521346 - FZÚ 2020 RIV US eng J - Článek v odborném periodiku
Guillemot, L. - Loiko, P. - Braud, A. - Doualan, J. L. - Hideur, A. - Košelja, Michal - Moncorgé, R. - Camy, P.
Continuous-wave Tm:YAlO3 laser at similar to 2.3 mu m.
Optics Letters. Roč. 44, č. 20 (2019), s. 5077-5080. ISSN 0146-9592. E-ISSN 1539-4794
Institucionální podpora: RVO:68378271
Klíčová slova: crystal * continuous wave * laser
Obor OECD: Optics (including laser optics and quantum optics)
Impakt faktor: 3.714, rok: 2019
Způsob publikování: Omezený přístup
https://doi.org/10.1364/ol.44.005077
The orthorhombic Tm 3+ :YAlO 3 Tm3+:YAlO3 crystal is promising for laser operation at the ???? 4 3 →???? 4 3 H43→F43 (1.5 μm) and ???? 4 3 →???? 5 3 H43→H53 (2.3 μm) transitions. Stimulated-emission cross-sections for these transitions are determined with polarized light. Peak values of 0.59×10 −20 cm 2 0.59×10−20 cm2 and 0.80×10 −20 cm 2 0.80×10−20 cm2 are found at 1438 nm and 2275 nm, respectively, both for ????∥???? E∥b . The cross-relaxation defining the upper-laser level lifetime is quantified. Continuous-wave lasing at the ???? 4 3 →???? 5 3 H43→H53 transition is achieved with an ???? a -cut 1.5 at.% Tm:YAlO 3 Tm:YAlO3 crystal. The laser generated 254 mW at 2273 nm with a slope efficiency of 17.8% and linear polarization.