Carbon materials derived from poly(aniline-co-p-phenylenediamine) cryogels

0518286 - ÚMCH 2021 RIV CH eng J - Článek v odborném periodiku
Milakin, Konstantin A. - Gavrilov, N. - Pašti, I. A. - Trchová, Miroslava - Zasońska, Beata Anna - Stejskal, Jaroslav - Bober, Patrycja
Carbon materials derived from poly(aniline-co-p-phenylenediamine) cryogels.
Polymers. Roč. 12, č. 1 (2020), s. 1-11, č. článku 11. E-ISSN 2073-4360
Grant CEP: GA ČR(CZ) GA18-04669S
Institucionální podpora: RVO:61389013
Klíčová slova: poly(aniline-co-p-phenylenediamine) * cryogels * carbonization
Obor OECD: Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics
Impakt faktor: 4.329, rok: 2020
Způsob publikování: Open access
https://www.mdpi.com/2073-4360/12/1/11

Nitrogen-containing carbon derivatives were prepared by the carbonization of poly(aniline-co-p-phenylenediamine) cryogels in inert atmosphere. Lower aniline fraction in the comonomer mixture used for preparation of the cryogels led to the decrease of their thermal stability, a consequent increase of carbonization degree, and less defective structure of carbonized materials. The resulting carbonaceous products had up to 4 orders of magnitude higher specific surface area than their respective cryogel precursors, the highest value 931 m2 g−1 being achieved for carbonized poly(p-phenylenediamine) cryogel. Electrochemical characterization of the carbon derivatives demonstrated that the decrease in aniline concentration during the synthesis of the precursor cryogels led to higher gravimetric capacitance for corresponding carbonized materials. These materials can potentially be used for energy storage applications.
Trvalý link: http://hdl.handle.net/11104/0306206