X-ray micro-tomography characterization of voids caused by three-point bending in selected alkali-activated aluminosilicate composite

0517648 - ÚTAM 2020 RIV CZ eng C - Konferenční příspěvek (zahraniční konf.)
Kumpová, Ivana - Rozsypalová, I. - Keršner, Z. - Rovnaníková, P. - Vopálenský, Michal
X-ray micro-tomography characterization of voids caused by three-point bending in selected alkali-activated aluminosilicate composite.
Acta Polytechnica CTU Proceedings. Vol. 25. Praha: Czech Technical University in Prague, 2019 - (Kytýř, D.; Zlámal, P.; Doktor, T.), s. 58-63. ISBN 978-80-01-06670-6.
[Youth Symposium on Experimental Solid Mechanics /17./. Telč (CZ), 06.06.2019-08.06.2019]
Institucionální podpora: RVO:68378297
Klíčová slova: alkali-activated aluminosilicate composite * fracture surface * X-ray micro-tomography * 3D porosity evaluation * fractal dimension
Obor OECD: Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics
https://ojs.cvut.cz/ojs/index.php/APP/article/view/6026

This paper deals with the pilot characterization of a special alkali-activated aluminosilicate composite composed of waste brick powder, brick rubble and a solution of potassium water glass. Fracture tests were conducted on the specimens via three-point bending and fracture parameters were evaluated. Selected specimen was investigated using micro-tomography to supplement the results with visual information about the inner structure of this newly designed material before and after the mechanical loading. Tomographic measurements and image processing were conducted for a qualitative and quantitative assessment of changes in the internal structure with an emphasis on the calculation of porosimetric parameters and visualization of the fracture surface. Fractal dimension of fracture surface was estimated.